摘要
CeO_2 hollow spheres were synthesized by polystryrene sphere（PS） templates and CeO_2 nanoparticles were prepared by a facile method. The as-obtained products were characterized by scanning electron microscopy（SEM）, N_2 adsorption-desorption, X-ray diffraction（XRD）, Fourier transform infrared spectroscopy（FTIR） and UV-vis diffuse reflectance spectra. The results showed that the structure of the obtained CeO_2 hollow spheres was hollow microsphere with a diameter of 380 nm and the average particle size of CeO_2 nanoparticles was about 1700 nm. The two samples＇ Brunauer-Emmett-Teller（BET） surface area was 67.1 and 37.2 m^2/g. The CeO_2 hollow spheres had a better performance than nanoparticles at UV-shielding because of higher surface area and the structure of hollow sphere.
CeO_2 hollow spheres were synthesized by polystryrene sphere（PS） templates and CeO_2 nanoparticles were prepared by a facile method. The as-obtained products were characterized by scanning electron microscopy（SEM）, N_2 adsorption-desorption, X-ray diffraction（XRD）, Fourier transform infrared spectroscopy（FTIR） and UV-vis diffuse reflectance spectra. The results showed that the structure of the obtained CeO_2 hollow spheres was hollow microsphere with a diameter of 380 nm and the average particle size of CeO_2 nanoparticles was about 1700 nm. The two samples＇ Brunauer-Emmett-Teller（BET） surface area was 67.1 and 37.2 m^2/g. The CeO_2 hollow spheres had a better performance than nanoparticles at UV-shielding because of higher surface area and the structure of hollow sphere.
基金
supported by the Capacity Building Program of Shanghai Local Universities(12160503600)