CdS quantum dots sensitized platelike WO_3 photoelectrodes were successfully synthesized by a facile hydrothermal method and a modified chemical bath deposition(CBD) technique.To further improve the stability of the photoelectrodes in alkaline environment,the platelike WO_3 films were treated with TiCl_4 to form a nano-TiO_2 buffer layer on the WO_3 plate surface before loading CdSQDs.The resulting electrodes were characterized by using XRD,SEM,HR-TEM and UV-vis spectrum.The photocatalytic activity of the resulting electrodes was investigated by degradation of methyl orange(MO) in aqueous solution.The photoelectrochemical(PEC) property of the resulting electrodes was also characterized by the linear sweep voltammetry.The results of both the degradation of MO and photocurrent tests indicated that the as-prepared CdSQDs sensitized WO_3 platelike photoelectrodes exhibit a significant improvement in photocatalytic degradation and PEC activity under visible light irradiation,compared with unsupported CdSQDs electrodes.Significantly,coating the WO_3 plates with nano-TiO_2 obviously facilitate the charge separation and retards the charge-pair recombination,and results in a highest activity for QDsCdS/TiO_2/WO_3 photoelectrodes.
CdS quantum dots sensitized platelike WO3 photoelectrodes were successfully synthesized by a facile hydrothermal method and a modified chemical bath deposition(CBD) technique.To further improve the stability of the photoelectrodes in alkaline environment,the platelike WO3 films were treated with TiCl4 to form a nano-TiO2 buffer layer on the WO3 plate surface before loading CdSQDs.The resulting electrodes were characterized by using XRD,SEM,HR-TEM and UV-vis spectrum.The photocatalytic activity of the resulting electrodes was investigated by degradation of methyl orange(MO) in aqueous solution.The photoelectrochemical(PEC) property of the resulting electrodes was also characterized by the linear sweep voltammetry.The results of both the degradation of MO and photocurrent tests indicated that the as-prepared CdSQDs sensitized WO3 platelike photoelectrodes exhibit a significant improvement in photocatalytic degradation and PEC activity under visible light irradiation,compared with unsupported CdSQDs electrodes.Significantly,coating the WO3 plates with nano-TiO2 obviously facilitate the charge separation and retards the charge-pair recombination,and results in a highest activity for QDsCdS/TiO2/WO3 photoelectrodes.
基金
Project(2014FJ3041)supported by the Research Funds of Science and Technology Agency of Hunan Provincial,China
Project(14A076)supported by the Research Funds of Education Agency of Hunan Provincial,China
Project supported by the Postdoctoral Science Foundation of Central South University,China