摘要
The hot deformation behavior and microstructure evolution of high manganese transformation induced plasticity steel(Fe - 20Mn - 3Si - 3Al) were investigated by using hot compression test in a temperature range from 800℃to 1 050℃and strain rate ranging from 0.01 s^(-1) to 5.0 s^(-1).The effects of temperature,strain rate,and true strain on the flow behavior and microstructures of high manganese transformation induced plasticity steel were discussed.The results show that the dynamic recrystallization occurs only at higher temperature and lower strain rate.Hot deformation behaviors of high manganese transformation induced plasticity steel were sensitive to temperature and strain rate.The apparent stress exponent and the apparent activation energy of the investigated steel were about 4.280 and 463.791 kJ/mol, respectively.The apparent activation energy of the high manganese transformation induced plasticity steel was approached to the austenitic stainless steel(400 -500 kJ/mol).The hot working equation is obtained. Hot deformation peak stress increased with increasing of the value of lnZ.Peak stress and InZ exhibits a linear variation,the linear correlation coefficient was 0.988 9.The results show that the dynamic recrystallization was prone to occur when lnZ≤43.842 26 and Z≤1.098×10^(19),and better hot deformation properties would be obtained under this condition.
The hot deformation behavior and microstructure evolution of high manganese transformation induced plasticity steel(Fe - 20Mn - 3Si - 3Al) were investigated by using hot compression test in a temperature range from 800℃to 1 050℃and strain rate ranging from 0.01 s^(-1) to 5.0 s^(-1).The effects of temperature,strain rate,and true strain on the flow behavior and microstructures of high manganese transformation induced plasticity steel were discussed.The results show that the dynamic recrystallization occurs only at higher temperature and lower strain rate.Hot deformation behaviors of high manganese transformation induced plasticity steel were sensitive to temperature and strain rate.The apparent stress exponent and the apparent activation energy of the investigated steel were about 4.280 and 463.791 kJ/mol, respectively.The apparent activation energy of the high manganese transformation induced plasticity steel was approached to the austenitic stainless steel(400 -500 kJ/mol).The hot working equation is obtained. Hot deformation peak stress increased with increasing of the value of lnZ.Peak stress and InZ exhibits a linear variation,the linear correlation coefficient was 0.988 9.The results show that the dynamic recrystallization was prone to occur when lnZ≤43.842 26 and Z≤1.098×10^(19),and better hot deformation properties would be obtained under this condition.