selecting several typical DSS 00Cr22Ni5Mo3N,00Cr21Ni2Mn5N and 00Cr25Ni7Mo4N as research materials,hot ductility characteristic of DSS was studied and microstructure evolution during hot compression was observed.The results show that the optimum hot ductility temperature range of DSS is 1 050~1 200℃.00Cr25Ni7Mc4N exhibits the worst hot ductility and 00Cr21Ni2Mn5N has similar hot ductility to 00Cr22Ni5Mo3N.During hot compression,austenite of DSS mainly occurs dynamic recovery,the ferrite of 00Cr22Ni5Mo3N,00Cr21Ni2Mn5N can perform dynamic recovery and recrystallization,but only dynamic recovery can be observed in the ferrite of 00Cr25Ni7Mo4N.
selecting several typical DSS 00Cr22Ni5Mo3N,00Cr21Ni2Mn5N and 00Cr25Ni7Mo4N as research materials,hot ductility characteristic of DSS was studied and microstructure evolution during hot compression was observed.The results show that the optimum hot ductility temperature range of DSS is 1 050~1 200℃.00Cr25Ni7Mc4N exhibits the worst hot ductility and 00Cr21Ni2Mn5N has similar hot ductility to 00Cr22Ni5Mo3N.During hot compression,austenite of DSS mainly occurs dynamic recovery,the ferrite of 00Cr22Ni5Mo3N,00Cr21Ni2Mn5N can perform dynamic recovery and recrystallization,but only dynamic recovery can be observed in the ferrite of 00Cr25Ni7Mo4N.