The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a single family of Ni_4Ti_3 precipitates with two crystallographically equivalent variants was formed after aging under compressive stress.Stressassisted aging resulted in tensile two-way shape memory effect strain of 1.56% under-5 MPa.Thermal cycling under-600 MPa resulted in a transformation strain of-2.15%,while the subsequent thermal cycling under-5 MPa resulted in a tensile two-way shape memory effect strain of 2.2%.
The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a single family of Ni_4Ti_3 precipitates with two crystallographically equivalent variants was formed after aging under compressive stress.Stressassisted aging resulted in tensile two-way shape memory effect strain of 1.56% under-5 MPa.Thermal cycling under-600 MPa resulted in a transformation strain of-2.15%,while the subsequent thermal cycling under-5 MPa resulted in a tensile two-way shape memory effect strain of 2.2%.
基金
supported in part by the NASA Fundamental Aeronautics Program
Supersonics Project and the NASA EPSCOR program(Grant No.NNX11AQ31A)
RFBR Project(Grant No.10-03-0154-a)