摘要
The interaction mechanism and phase evolution of ammonium polyphosphate（APP）mixed with muscovite（APP/muscovite）were studied by TG,XRD and SEM,respectively,during heating.When the temperature is not higher than 300 ℃,muscovite has no effect on the thermaldecomposition of APP,and the initialdecomposition temperature of APP/muscovite at 283 ℃ is basically the same as the APP at 295 ℃,and the main thermaldecomposition products are polyphosphoric acid and NH_4H_2PO_4 at 300 ℃.The polyphosphoric acid,the decomposition products of APP,can enable K and Siout of muscovite and interact with muscovite chemically to generate Al_2O_3·2SiO_2,α-SiO_2 and phosphates（AlPO_4 and K_5P_3O_（10））compounds during 400 ℃-800 ℃,which own obvious adhesive phenomenon and porous structure with the apparent porosity of 58.4%.Further reactions between phosphates other than reactions among Al_2O_3·2SiO_2 and α-SiO_2 can generate KAlP_2O_7 at 1 000 ℃ and the density of residualproduct is improved by low melting point phosphate filling pore to form relatively dense structure and decrease the apparent porosity to 44.4%.The flame resistant and self-supported ceramic materials are expected to enhance the fire-retarding synergistic effect between APP and muscovite.
The interaction mechanism and phase evolution of ammonium polyphosphate（APP）mixed with muscovite（APP/muscovite）were studied by TG,XRD and SEM,respectively,during heating.When the temperature is not higher than 300 ℃,muscovite has no effect on the thermaldecomposition of APP,and the initialdecomposition temperature of APP/muscovite at 283 ℃ is basically the same as the APP at 295 ℃,and the main thermaldecomposition products are polyphosphoric acid and NH_4H_2PO_4 at 300 ℃.The polyphosphoric acid,the decomposition products of APP,can enable K and Siout of muscovite and interact with muscovite chemically to generate Al_2O_3·2SiO_2,α-SiO_2 and phosphates（AlPO_4 and K_5P_3O_（10））compounds during 400 ℃-800 ℃,which own obvious adhesive phenomenon and porous structure with the apparent porosity of 58.4%.Further reactions between phosphates other than reactions among Al_2O_3·2SiO_2 and α-SiO_2 can generate KAlP_2O_7 at 1 000 ℃ and the density of residualproduct is improved by low melting point phosphate filling pore to form relatively dense structure and decrease the apparent porosity to 44.4%.The flame resistant and self-supported ceramic materials are expected to enhance the fire-retarding synergistic effect between APP and muscovite.
基金
Funded by the National Natural Science Foundation of China(No.51472188)