Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss.
Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss.
基金
Funded by the National Natural Science Foundation of China(Nos.51174057 and 51404159)
the National High Technology Research and Development Program(No.2012AA03A503)
Research Fund for the Doctoral Program of Higher Education of China(No.20130042110040)