摘要
研究了聚羧酸减水剂品种(丙烯酸系和马来酸系)对混凝土电通量、内部相对湿度、失水率以及混凝土微观结构的影响。结果表明:掺有丙烯酸系减水剂的混凝土抵抗氯离子的渗透能力高于掺有马来酸系减水剂混凝土,其内部相对湿度降低速率高于马来酸系减水剂混凝土以及失水速率低于马来酸系减水剂混凝土;掺有丙烯酸系减水剂的混凝土微观结构较密实,孔隙率较低,孔径较小。
The influences of polycarboxylate superplasticizer(acrylic and maleic acid system) on electric flux, internal relative humidity and water loss rate were studied. The results show that the penetration ability that resistance to chloride ion of concrete adding the acrylic acid superplasticizer is higher than that of mixed with maleic acid series superplasticizer, and the internal relative humidity decrease rate is higher than that of maleic acid series superplasticizer concrete, and its water loss rate is lower than the maleic acid superplasticizer in concrete.Mercury analysis results showed that the microstructure of concrete mixed with acrylic acid superplasticizer is more compact,lower porosity and smaller pore size.
出处
《河北交通职业技术学院学报》
2016年第1期42-45,共4页
Journal of Hebei Jiaotong Vocational and Technical College
关键词
聚羧酸减水剂
混凝土
渗透性
作用机理
polycarboxylic water reducing agent
concrete
permeability
interaction mechanism