A well core-shell composite of Y@meso-Al with a mesoporous alumina shell and a Y zeolite core was synthesized. The mesoporous alumina shell has a wormhole-like structure with large mesopores. The prepared catalytic cracking catalyst using this composite has exhibited excellent catalytic performance for heavy oil cracking thanks to its favorable physicochemical properties, such as high surface area, large pore volume and outstanding acid sites accessibility for large molecules provided by the composite. In comparison with the reference catalyst using pure Y zeolite, the oil conversion achieved by the above-mentioned catalyst increased by 2.73 percentage points, while the heavy oil yield and coke yield decreased by 2.23 percentage points and 1.28 percentage points, respectively, with the light oil yield increasing by 2.27 percentage points.
A well core-shell composite of Y@meso-Al with a mesoporous alumina shell and a Y zeolite core was synthesized. The mesoporous alumina shell has a wormhole-like structure with large mesopores. The prepared catalytic cracking catalyst using this composite has exhibited excellent catalytic performance for heavy oil cracking thanks to its favorable physicochemical properties, such as high surface area, large pore volume and outstanding acid sites accessibility for large molecules provided by the composite. In comparison with the reference catalyst using pure Y zeolite, the oil conversion achieved by the above-mentioned catalyst increased by 2.73 percentage points, while the heavy oil yield and coke yield decreased by 2.23 percentage points and 1.28 percentage points, respectively, with the light oil yield increasing by 2.27 percentage points.
基金
financially supported by the Department of Science and Technology Management of Petro China (No. 2011B-2404-0102)