摘要
Two 3D 4-fold interpenetrated metal-organic frameworks, [Mn（L）（bpy）]n （1） and [Cu（HL）（bpy）]n （2）（H3L = 4,4＇,4＇＇-（benzene-1,3,5-triyl-tri（methyleneoxy）） tribenzoic acid, bpy = 4,4′-bipyridine）, were synthesized under hydrothermal conditions, and characterized by element analyses, IR spectra, thermogravimetric analyses, X-ray powder diffraction and magnetic property studies. The single-crystal X-ray analyses revealed that 1 and 2 are homogeneous. 1 crystallizes in monoclinic, space group Cc with a = 26.794（2）, b = 11.6346（10）, c = 21.4614（18） ？, β = 91.570（2）°, V = 6687.9（10） A^3, Z = 8, Mr = 736.59, D = 1.463 g·cm^（-3）, μ = 0.458 mm^-1c, R（int） = 0.0524, F（000） = 3040, the final R = 0.0844 and wR = 0.2266 for 8092 observed reflections（I 〉 2σ（I））. 2 crystallizes in monoclinic, space group Cc with a = 27.609（12）, b = 11.126（10）, c = 21.490（9） ？, β = 92.131（2）°, V = 6597（5） A^3, Z = 8, Mr = 746.21, Dc = 1503 g·cm^（-3）, μ = 0.726 mm^-1, R（int） = 0.0542, F（000） = 3080, the final R =0.0681 and wR = 0.1831 for 6777 observed reflections（I 〉 2σ（I））. Two compounds are 3D [2＋2]-type 4-fold interpenetrated frameworks with（6^3）（6^9.8） hms topology. The magnetic study of compound 2 shows the presence of weak antiferromagnetic interaction between the Cu^Ⅱ ions in 2.
Two 3D 4-fold interpenetrated metal-organic frameworks, [Mn（L）（bpy）]n （1） and [Cu（HL）（bpy）]n （2）（H3L = 4,4＇,4＇＇-（benzene-1,3,5-triyl-tri（methyleneoxy）） tribenzoic acid, bpy = 4,4′-bipyridine）, were synthesized under hydrothermal conditions, and characterized by element analyses, IR spectra, thermogravimetric analyses, X-ray powder diffraction and magnetic property studies. The single-crystal X-ray analyses revealed that 1 and 2 are homogeneous. 1 crystallizes in monoclinic, space group Cc with a = 26.794（2）, b = 11.6346（10）, c = 21.4614（18） ？, β = 91.570（2）°, V = 6687.9（10） A^3, Z = 8, Mr = 736.59, D = 1.463 g·cm^（-3）, μ = 0.458 mm^-1c, R（int） = 0.0524, F（000） = 3040, the final R = 0.0844 and wR = 0.2266 for 8092 observed reflections（I 〉 2σ（I））. 2 crystallizes in monoclinic, space group Cc with a = 27.609（12）, b = 11.126（10）, c = 21.490（9） ？, β = 92.131（2）°, V = 6597（5） A^3, Z = 8, Mr = 746.21, Dc = 1503 g·cm^（-3）, μ = 0.726 mm^-1, R（int） = 0.0542, F（000） = 3080, the final R =0.0681 and wR = 0.1831 for 6777 observed reflections（I 〉 2σ（I））. Two compounds are 3D [2＋2]-type 4-fold interpenetrated frameworks with（6^3）（6^9.8） hms topology. The magnetic study of compound 2 shows the presence of weak antiferromagnetic interaction between the Cu^Ⅱ ions in 2.
基金
Supported by the Education Committee of Sichuan Province(12ZA090,13CZ0019 and 14ZB0220)
Key Laboratory of Green Catalysis of Sichuan Institutes of High Education(LZJ14201)
Sichuan University of Science and Engineering(Y2014018)