硅藻土/β-环糊精复合高吸水树脂的研究

Study of diatomite/β-cyclodextrin complex superabsorbent resin

采用水溶液聚合法,以N,N-亚甲基双丙烯酰胺(NMBA)为交联剂,过硫酸钾(KPS)为引发剂,在丙烯酸(AA)和丙烯酰胺(AM)共聚交联反应的基础上添加一定比例的硅藻土和β-环糊精(β-CD),制备硅藻土/β-环糊精复合高吸水树脂。考察了硅藻土与β-环糊精的质量比、单体质量比、交联剂的用量、引发剂用量、反应温度和丙烯酸中和度对复合树脂吸水率的影响。实验结果表明,当m(硅藻土)∶m(β-环糊精)=1∶3,m(AA):m(AM)=5∶1,w(交联剂)=0.04%,w(引发剂)=0.3%,反应温度T=75℃,AA中和度为70%时,复合高吸水树脂最大吸水率为783 g·g^(-1),最大吸盐水率为85 g·g^(-1)。

A superabsorbent resin was synthesized in N, N-methylene bis-acrylamide （NMBA） as crosslinker, potassium persulfate （KPS） as initiator, the acrylic （AA） and acrylamide （AM） copol- ymerization crosslinking reaction add a certain percentage based on the β-cyclodextrin and diatomite, synthetic diatomite/β-cyclodextrin superabsorbent composite. Effects of reaction temperature, diatom- ite and 13-cyclodextrin mass ratio, acrylic acid neutralization degrees, the amount of initiator, the im- pact composite resin crosslinking agent for water absorption are investigated. Experimental results show that： whenm （diatomite） ： m（β-cyclodextrin） = 1 ： 3, m （AA） ： m（AM） = 5 ： 1, w （ crosslinking agent） = 0. 04%, w （initiator） = 0. 3%, the reaction temperature T = 75℃, AA degree of neutralization 70%, the corresponding composite superabsorbent maximum absorbency is 783g·g , the maximum absorption rate of saline is 85g · g-1.