In this work,Raman scattering measurements have been performed on the collapsed phase CaCo2As2 crystals.At least 8 Raman modes were observed at room temperature though CaCo2As2 is structurally similar to other 122 compounds like BaFe2As2.Two Raman modes are assigned to the intrinsic A1gand B1gof this material system respectively.The other ones are considered to originate from the local vibrations relevant to cobalt vacancies.Careful polarized measurements allow us to clearly resolve the four-fold symmetry of the B1gmode,which put strong constraints on possible point group symmetries of the system with Co vacancies.The temperature-dependent measurements demonstrate that the anomalies in both frequency and width of the B1gmode occur around Neel temperature TN.The anomalies are considered to be related to the gap opening near the magnetic transition.The study may shed light on the structural and magnetic changes and their correlations with superconductivity in 122 systems.
In this work,Raman scattering measurements have been performed on the collapsed phase CaCo2As2 crystals.At least 8 Raman modes were observed at room temperature though CaCo2As2 is structurally similar to other 122 compounds like BaFe2As2.Two Raman modes are assigned to the intrinsic A1gand B1gof this material system respectively.The other ones are considered to originate from the local vibrations relevant to cobalt vacancies.Careful polarized measurements allow us to clearly resolve the four-fold symmetry of the B1gmode,which put strong constraints on possible point group symmetries of the system with Co vacancies.The temperature-dependent measurements demonstrate that the anomalies in both frequency and width of the B1gmode occur around Neel temperature TN.The anomalies are considered to be related to the gap opening near the magnetic transition.The study may shed light on the structural and magnetic changes and their correlations with superconductivity in 122 systems.
基金
Project supported by the National Basic Research Program of China(Grant No.2012CB921701)
the National Natural Science Foundation of China(Grant No.11474357)
the Fundamental Research Funds for the Central Universities
the Research Funds of Renmin University of China