基于磁感应强度的25Cr35NiNb+MA裂解炉管渗碳检测研究 被引量:3

Study on Detection of Pyrolysis Furnace Tubes Carburization Based on Magnetic Flux Intensity
下载PDF
导出
摘要 采用基于磁感应强度变化原理的渗碳检测仪,对服役后不同渗碳程度的25Cr35Ni Nb+MA材质乙烯裂解炉管进行磁感应强度检测,通过系列理化试验,对上述炉管渗碳层厚度进行检测。检测结果表明:针对25Cr35Ni Nb+MA材质乙烯裂解炉管,采用渗碳检测仪的磁感应强度检测输出值与炉管渗碳层厚度之间具有良好的对应关系,为渗碳检测仪对在役乙烯裂解炉管渗碳层厚度的检测提供依据。同时,还对不同渗碳层厚度25Cr35Ni Nb+MA材质乙烯裂解炉管不同部位典型组织进行了表征。 By using carburizing testers based on the principle of magnetic flux intensity variation,the magnetic flux intensity of 25Cr35 Ni Nb + MA material ethylene pyrolysis furnace tubes with different degrees of carburization after service were detected. Through a series of physical and chemical tests,carburizing layer thickness of furnace tubes above were detected. The relationship between the magnetic flux intensity and carburized layer thickness of typical material ethylene pyrolysis furnace tubes was established initially,which provides basis for the carburized layer thickness detection of ethylene pyrolysis furnace tubes in service by carburizing testers. The typical microstructure of 25Cr35 Ni Nb + MA ethylene pyrolysis furnace tubes at different parts with different thickness of carburized layer was characterized in this paper.
出处 《压力容器》 2016年第5期56-61,共6页 Pressure Vessel Technology
基金 国家高技术研究发展计划(863计划)资助(2015AA034402)
关键词 乙烯裂解炉管 渗碳 磁感应强度 25Cr35NiNb+MA ethylene pyrolysis furnace tubes carburization magnetic flux intensity 25Cr35NiNb + MA
  • 相关文献

参考文献13

  • 1Almeida L H, Ribeiro A F, May I L Microstructural characterization of modified 25Cr - 35Ni centrifugallycast steel furnace tubes [ J ]. Materials Characteriza- tion,2002,49 ( 3 ) : 219 - 229.
  • 2Kenik E A, Maziasz P J,Swindeman R W, et al. Struc- ture and phase stability in a cast modified - HP austen- ire 'after long - term ageing [ J ]. Scripta Materialia, 2003,49(2) :117 - 122.
  • 3Kaya A A. Microstructure of HK40 alloy after high - temperature service in oxidizing or carburizing envion- ment I]. Carburization and carbide transformations [ J ]. Materials Characterization ,2002,49 ( 1 ) :23 - 34.
  • 4陈涛,陈学东,吕运容,艾志斌,范志超.国产乙烯裂解炉管抽样检测状况[J].压力容器,2014,31(3):45-55. 被引量:13
  • 5连晓明,陈学东,吕运容,陈涛.高温时效对25Cr35Ni-Nb合金碳化物的影响[J].压力容器,2011,28(8):1-5. 被引量:19
  • 6Wu X Q,Yang Y S,Zhan Q,et al. Stucmre degrada- tion of HP cracking tuhe during service [ J ]. Acta Ma- tallurgica Siniea, 1998,34 : 1043 - 1048.
  • 7Takahashi S, Sato Y, Kamada Y, et al. Study of chromi- um depletion by magnetic method in Ni - based alloys [J ]. Journal of Magnetism & Magnetic Materials, 2004,269(2) : 139 - 149.
  • 8Grabke I4 J, Wolf I. Carburization and oxidation [ ] ]. Material Science Engineering, 1997,87:23 - 33.
  • 9吴建平.乙烯裂解炉辐射段炉管失效原因分析及对策[J].石油和化工设备,2013,16(8):30-33. 被引量:7
  • 10SHS03001-2004,管式裂解炉维护检修规程[S].

二级参考文献50

共引文献32

同被引文献26

引证文献3

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部