Laser powder deposition was applied to fabricate the Ti-6.5Al-3.5Mo-1.5Zr-0.3Si （wt%）/Ti-47Al- 2Cr-2Nb-0.2W-0.15B （at%） bi-material system. The asdeposited TC11 alloy shows a basket-wave-like morphology while the as-deposited y-TiAl alloy consists of fully α2/γ lamellar microstructures. Regarding the thermal mismatch between TC11 and γ-TiAl during processing, the interface microstmcture evolution was concerned. The transformation pathway was illustrated. It is found that the content changes of Al elements and β-stabilizers Mo, Cr, and Nb are responsible for the evolution of microstructures at the interface. The fracture surfaces are located at the y-TiAl side. The bi-material shows a brittle-fracture manner, with the ultimate tensile strength of 560 MPa.
Laser powder deposition was applied to fabricate the Ti-6.5Al-3.5Mo-1.5Zr-0.3Si （wt%）/Ti-47Al- 2Cr-2Nb-0.2W-0.15B （at%） bi-material system. The asdeposited TC11 alloy shows a basket-wave-like morphology while the as-deposited y-TiAl alloy consists of fully α2/γ lamellar microstructures. Regarding the thermal mismatch between TC11 and γ-TiAl during processing, the interface microstmcture evolution was concerned. The transformation pathway was illustrated. It is found that the content changes of Al elements and β-stabilizers Mo, Cr, and Nb are responsible for the evolution of microstructures at the interface. The fracture surfaces are located at the y-TiAl side. The bi-material shows a brittle-fracture manner, with the ultimate tensile strength of 560 MPa.
基金
financially supported by the National Basic Research Development Program of China(No.2011CB606305)