摘要
Carboxymethyl cellulose(CMC) fibers were produced by extruding the CMC solution into the metal salt coagulation bath and collected with a winding machine.It was found that copper chloride,ferric chloride,cerium chloride,lanthanum chloride and aluminum nitrate solution could be used as coagulation bath to prepare CMC fibers,whereas the metal salt solutions,such as nickel chloride,zinc chloride,calcium chloride and magnesium chloride,could not.The fiber formation is due to the coordination between the carboxylates of CMC and metal ion.Fourier transform infrared spectroscopy(FTIR) was applied to studying the coordination mode of CMC and metal ion.The metal salt concentration,pH value and temperature of the coagulation bath affect the tenacity and elongation of the fiber.CMC fibers show good water uptake ability and can adsorb water more than 200% of its own weight.The mechanical behaviors of CMC fiber show dependence on environment humidity.
Carboxymethyl cellulose（CMC） fibers were produced by extruding the CMC solution into the metal salt coagulation bath and collected with a winding machine.It was found that copper chloride,ferric chloride,cerium chloride,lanthanum chloride and aluminum nitrate solution could be used as coagulation bath to prepare CMC fibers,whereas the metal salt solutions,such as nickel chloride,zinc chloride,calcium chloride and magnesium chloride,could not.The fiber formation is due to the coordination between the carboxylates of CMC and metal ion.Fourier transform infrared spectroscopy（FTIR） was applied to studying the coordination mode of CMC and metal ion.The metal salt concentration,pH value and temperature of the coagulation bath affect the tenacity and elongation of the fiber.CMC fibers show good water uptake ability and can adsorb water more than 200% of its own weight.The mechanical behaviors of CMC fiber show dependence on environment humidity.
基金
National Natural Science Foundation of China(No.51373032)
Innovation Program of Shanghai Municipal Education Commission,China
Fundamental Research Funds for the Central University,China
DHU Distinguished Young Professor Program,China