A series of KY3F10 nanophosphors doped with Gd3＋, Ce3＋ and Eu3＋ ions were obtained with the use of a co-precipitation method. The resulting products were white precipitates, consisting of spherical particles with diameter about 150-200 nm, which was confirmed using transmission electron microscopy （TEM） technique. Powder X-ray diffraction （XRD） and energy dispersive X-ray analysis （EDX） measurements confirmed appropriate structures of the nanoparticles obtained. Spectroscopic properties of the prod- ucts were examined on the basis of the measured excitation/emission spectra and luminescence decay curves. The synthesized sam- ples showed orange-red luminescence, characteristic for Eu3＋ ions. The reaction process was performed in required alkaline pH ad- justed with the use of ethylenediaminetetraacetic acid （EDTA） and potassium hydroxide. The samples containing large amounts of Gd3＋ dooant ions exhibited a tendencv to form nroducts with different momhologies.
A series of KY3F10 nanophosphors doped with Gd3＋, Ce3＋ and Eu3＋ ions were obtained with the use of a co-precipitation method. The resulting products were white precipitates, consisting of spherical particles with diameter about 150-200 nm, which was confirmed using transmission electron microscopy （TEM） technique. Powder X-ray diffraction （XRD） and energy dispersive X-ray analysis （EDX） measurements confirmed appropriate structures of the nanoparticles obtained. Spectroscopic properties of the prod- ucts were examined on the basis of the measured excitation/emission spectra and luminescence decay curves. The synthesized sam- ples showed orange-red luminescence, characteristic for Eu3＋ ions. The reaction process was performed in required alkaline pH ad- justed with the use of ethylenediaminetetraacetic acid （EDTA） and potassium hydroxide. The samples containing large amounts of Gd3＋ dooant ions exhibited a tendencv to form nroducts with different momhologies.
基金
Project supported by the Polish National Science Centre(2015/17/N/ST5/01947)