Investigation on Phase Evolution of the ZnO-B2O3-SiO2 Glass Ceramics

Investigation on Phase Evolution of the ZnO-B_2O_3-SiO_2 Glass Ceramics
下载PDF
导出
摘要 ZnO-B2O3-SiO2-Al2O3-Na2O glass doped with nucleating agent TiO2 was prepared with melting-quenching method and the effect of nucleating agent on the crystallization behavior and phase evolution of this glass was investigated by differential thermal analysis(DTA),X-ray diffraction(XRD),and scanning electron microscopy(SEM).The experimental results show that the glass transition temperature and the first crystallization temperature decrease from 630 ℃ and 765 ℃ to 595 ℃ and 740 ℃,respectively,with introduction of TiO2 into glass.There is no diffraction peaks in the XRD pattern but it is no longer transparent for the base glass without nucleating agent after heat treatment,which suggests the serious phase separation occurred,and the observation by SEM indicates that the phase separation is developed by nucleation and growth mechanism.However,there are two different crystals ZnAl2O4 and NaAlSiO4 present in the glass containing TiO2 after heat treating at 575 ℃ for 2 h and 740 ℃ for 6 h,respectively.What is interesting is that NaAlSiO4 disappears as the crystallization time at 740 ℃ increases from 6 h to 12 h,and more ZnAl2O4 crystal is formed,namely,the further formation of ZnAl2O4 is at cost of NaAlSiO4 with increasing crystallization time.And observation of the morphology of glass ceramics shows great difference with increasing crystallization time.Moreover,the ability of ZnO-B2O3-SiO2-Al2O3-Na2O glass ceramics against attacking of 1M HCl solution is increased by the crystals precipitated in heat treatment process. ZnO-B2O3-SiO2-Al2O3-Na2O glass doped with nucleating agent TiO2 was prepared with melting-quenching method and the effect of nucleating agent on the crystallization behavior and phase evolution of this glass was investigated by differential thermal analysis(DTA),X-ray diffraction(XRD),and scanning electron microscopy(SEM).The experimental results show that the glass transition temperature and the first crystallization temperature decrease from 630 ℃ and 765 ℃ to 595 ℃ and 740 ℃,respectively,with introduction of TiO2 into glass.There is no diffraction peaks in the XRD pattern but it is no longer transparent for the base glass without nucleating agent after heat treatment,which suggests the serious phase separation occurred,and the observation by SEM indicates that the phase separation is developed by nucleation and growth mechanism.However,there are two different crystals ZnAl2O4 and NaAlSiO4 present in the glass containing TiO2 after heat treating at 575 ℃ for 2 h and 740 ℃ for 6 h,respectively.What is interesting is that NaAlSiO4 disappears as the crystallization time at 740 ℃ increases from 6 h to 12 h,and more ZnAl2O4 crystal is formed,namely,the further formation of ZnAl2O4 is at cost of NaAlSiO4 with increasing crystallization time.And observation of the morphology of glass ceramics shows great difference with increasing crystallization time.Moreover,the ability of ZnO-B2O3-SiO2-Al2O3-Na2O glass ceramics against attacking of 1M HCl solution is increased by the crystals precipitated in heat treatment process.
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2016年第4期830-834,共5页 武汉理工大学学报(材料科学英文版)
基金 Funded by the National Natural Science Foundation of Ch ina(51202104 and 51362019) the Natural Science Foundation of the Inner Mongolia Autonomous Region(2016JQ05) the Young Talents of Inner Mongolia Autonomous Region,Inner Mong olia University of Science and Technology(2014QNGG02)
关键词 nucleation ceramics melting transparent crystalline precipitated longer quenching heating attributed nucleation ceramics melting transparent crystalline precipitated longer quenching heating attributed
  • 相关文献

参考文献2

二级参考文献14

  • 1万军鹏,程金树,汤李缨.浅谈硼硅酸盐玻璃的应用现状和发展趋势[J].玻璃,2004,31(5):21-25. 被引量:20
  • 2ESCARDINO A, AMOROS J L, GOZALBO A, et al. Gahnite devitrification in ceramic frits, mechanism and process kinetics [J]. J Am Ceram Soc, 2000, 83(12) :2 938- 2 944.
  • 3PANDEY R, GALE J D, SAMPATH S K,et al. Atomistic simulation study of spinel oxides, zinc aluminate and zinc gallate[J]. J Am Ceram Soc, 1999, 82(12):3 337-3 341.
  • 4KASHII N, MAEKAWA H, HINATSU Y. Dynamics of the cation mixing of MgAl2O4 and ZnAl2O4 spinel[J]. J Am Ceram Soc, 1999, 82(7):1 844-1 848.
  • 5JESCHKE P, MORTL G. Recent tendencies in refractories for iron and steel production[A]. United International Technical Conference on Refractories(UNITECR)[C].San Paulo, Brazil, 1993. 26 -75.
  • 6LEVIN E, ROBBINS C R. Phase Diagrams for Ceramists[M].Columbus Ohio: American Ceramic Society, 1964. 258.
  • 7ROLSETH S, STOEN L, THONSTAD J. The solubility of ZnO and ZnAl2O4 in cryolite melts[J]. Metall Mater Trans B, 1997, 28:1 099-1 101.
  • 8TAKEUCHI N, TAKAHASHI H, ISHIDA S. Mechanistic study of solid-state reaction between kaolinite and ferrous oxide at high temperatures[J].J Ceram Soc Jpn, 2000. 108(10):876 - 861.
  • 9BRANSON D L. Kinetics and mechanism of the reaction between zinc oxide and aluminum oxide[J].J Am Ceram Soc,1965, 48(11): 591-595.
  • 10宋晓岚,屈一新,许超,蒋明慧.钛钡硼硅酸盐玻璃结构激光拉曼光谱研究[J].光散射学报,1998,10(1):30-36. 被引量:5

共引文献57

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部