The main objective was to study the anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating.Poly（o-toluidine）/nano ZrO2 composite was prepared by in situ polymerization of o-toluidine monomer in the presence of nano ZrO2 particles.Fourier transformation infrared spectroscopy（FT-IR）,UV-visible spectroscopy（UV-vis）,X-ray diffraction（XRD）,Scanning electron microscopy（SEM）,and Thermogravimetric analysis（TGA） were used to characterize the composition and structure of the composite.Poly（o-toluidine）/nano ZrO2 composite was mixed with epoxy resin through a solution blending method and the three components poly（o-toluidine）/nano ZrO2/epoxy composite coating was coated onto the surface of steel sample by the brush coating method.The anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating on steel sample was studied by polarization curve and electrochemical impendence spectroscopy in 3.5% Na Cl solution as corrosion environment and also compared with that of poly（o-toluidine）/epoxy composite coating and pure epoxy coating.It was observed that the composite coating containing poly（otoluidine）/nano ZrO2 composite has got higher corrosion protection ability than that of poly（o-toluidine）.The electrochemical measurement results demonstrated that poly（o-toluidine） fillers improve the electrochemical anticorrosion performance of epoxy coating and the addition of nano ZrO2 particles increases the tortuosity of the diffusion pathway of corrosive substances.
The main objective was to study the anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating.Poly（o-toluidine）/nano ZrO2 composite was prepared by in situ polymerization of o-toluidine monomer in the presence of nano ZrO2 particles.Fourier transformation infrared spectroscopy（FT-IR）,UV-visible spectroscopy（UV-vis）,X-ray diffraction（XRD）,Scanning electron microscopy（SEM）,and Thermogravimetric analysis（TGA） were used to characterize the composition and structure of the composite.Poly（o-toluidine）/nano ZrO2 composite was mixed with epoxy resin through a solution blending method and the three components poly（o-toluidine）/nano ZrO2/epoxy composite coating was coated onto the surface of steel sample by the brush coating method.The anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating on steel sample was studied by polarization curve and electrochemical impendence spectroscopy in 3.5% Na Cl solution as corrosion environment and also compared with that of poly（o-toluidine）/epoxy composite coating and pure epoxy coating.It was observed that the composite coating containing poly（otoluidine）/nano ZrO2 composite has got higher corrosion protection ability than that of poly（o-toluidine）.The electrochemical measurement results demonstrated that poly（o-toluidine） fillers improve the electrochemical anticorrosion performance of epoxy coating and the addition of nano ZrO2 particles increases the tortuosity of the diffusion pathway of corrosive substances.
基金
Funded by the Innovation Project of Guangxi Graduate Education(No.YCSZ2014202)