Foamable high melt strength polypropylene （HMSPP） was prepared by grafting styrene （St） onto polypropylene （PP） and simultaneously introducing poly- dimethylsiloxane （PDMS） through a one-step melt extru- sion process. The effect of PDMS viscosity on the foaming behavior of HMSPP was systematically investigated using supercritical CO2 as the foaming agent. The results show that the addition of PDMS has little effect on the grafting reaction of St and HMSPP exhibits enhanced elastic response and obvious strain hardening effect. Though the CO2 solubility of HMSPP with PDMS （PDMS-HMSPP） is lower than that of HMSPP without PDMS, especially for PDMS with low viscosity, the PDMS-HMSPP foams exhibit narrow cell size distribution and high cell density. The fracture morphology of PDMS-HMSPP shows that PDMS with low viscosity disperses more easily and uniformly in HMSPP matrix, leading to form small domains during the extrusion process. These small domains act as bubble nucleation sites and thus may be responsible for the improved foaming performance of HMSPP.
Foamable high melt strength polypropylene （HMSPP） was prepared by grafting styrene （St） onto polypropylene （PP） and simultaneously introducing poly- dimethylsiloxane （PDMS） through a one-step melt extru- sion process. The effect of PDMS viscosity on the foaming behavior of HMSPP was systematically investigated using supercritical CO2 as the foaming agent. The results show that the addition of PDMS has little effect on the grafting reaction of St and HMSPP exhibits enhanced elastic response and obvious strain hardening effect. Though the CO2 solubility of HMSPP with PDMS （PDMS-HMSPP） is lower than that of HMSPP without PDMS, especially for PDMS with low viscosity, the PDMS-HMSPP foams exhibit narrow cell size distribution and high cell density. The fracture morphology of PDMS-HMSPP shows that PDMS with low viscosity disperses more easily and uniformly in HMSPP matrix, leading to form small domains during the extrusion process. These small domains act as bubble nucleation sites and thus may be responsible for the improved foaming performance of HMSPP.
基金
Acknowledgements This work was financially supported by National Natural Science Foundation of China （Grant Nos. 21476085 and 21306047）, Fundamental Research Funds for the Central Universities of China （22A201514016
222201314051）.