摘要
采用XRD分析和充放电测试,研究氧化铝(Al_2O_3)掺杂量x对锂离子正极材料LiNi_(1/3)Co_(1/3-x)Mn_(1/3)Al_xO_2(x=0、1/40、1/20和1/10)性能的影响。当Al_2O_3掺杂量为1/20时,所得LiNi_(1/3)Co_(1/3-1/20)Mn_(1/3)Al_(1/20)O_2材料的结晶度较好且完整,混排度较低。以0.1 C在2.0~4.8 V充放电,正极材料的首次放电比容量为264.47 mAh/g,第20次循环的容量保持率为93.01%,库仑效率为98.37%。
XRD analysis and charge-discharge test were applied to investigate the effect of doped amount of aluminium oxide (AI203 )on the performance of L-ion battery cathode material LiNil/3Co1/3-xMn1/3 Alx O2 (x = 0,1/40,1/20 and 1/10). When the doped amount of AI203 was 1/20, the obtained material LiNil/3 COl/3-1/20 Mnl/3 All/20 02 had better crystallinity, the more complete crystal shape and the lower cation mixing. When charged-discharged in 2. 0 - 4. 8 V with 0. 1 C, its initial specific discharge capacity of the cathode material was 264.47 mAh/g, the capacity retention rate was 93.01% at the 20th cycle, the coulombic efficiency was 98. 37%.
出处
《电池》
CAS
CSCD
北大核心
2016年第4期197-199,共3页
Battery Bimonthly