生活垃圾开放式燃烧炭黑的结构及污染物分析 被引量:1

Microstructure and pollutant analysis of carbon black produced by municipal solid waste open-burning
下载PDF
导出
摘要 通过配置具有代表性的模拟城市生活垃圾,对模拟垃圾进行开放式燃烧并收集所产生的炭黑进行分析表征.利用扫描电子显微镜(SEM)、X射线光电子能谱仪(XPS)、比表面积及孔隙分析仪对炭黑进行微观颗粒形态的表征.结果显示,炭黑由粒径约为217.8nm的球形颗粒团聚形成,比表面积高达27.554m2/g,且表面有丰富的含氧、含氯官能团以及催化金属,具有非常高的反应活性.对炭黑颗粒中的多环芳烃以及二恶英类物质进行检测,结果显示,多环芳烃、二恶英的质量分数分别达到8.865×10-5和1.92×10-8.城市生活垃圾开放式燃烧所产生的炭黑以及其他气态污染物直接排放至大气中,对环境造成的危害须引起高度重视. A representative model municipal solid waste was prepared for open burning experiment.Carbon black was gathered and detailed characterization was done by means of scanning electron microscope(SEM),X-ray photoelectron spectroscopy(XPS)and specific surface area and pore analyzer.Carbon black is made up of small spherical particles,the particle diameter is about 217.8nm and specific surface area is up to 27.554m2/g.The carbon black shows high reactivity as abundant oxygen-containing and chlorinecontaining functional groups are detected as well as catalytic metal.The carbon produced from municipal solid waste open-burning contains abundant persistent organic pollutants,such as polychlorinated dibenzop-dioxins/dibenzofurans(PCDD/Fs)and polycyclic aromatic hydrocarbons(PAHs).The mass fraction of PAHs and PCDD/Fs in carbon black is up to 8.865×10-5 and 1.92×10-8.As the carbon black produced from municipal solid waste open-burning is directly released to the environment,as well as other gas phase pollutant,more attention should be paid on its harm to the environment.
出处 《浙江大学学报(工学版)》 EI CAS CSCD 北大核心 2016年第10期1849-1854,共6页 Journal of Zhejiang University:Engineering Science
基金 浙江省自然科学基金杰出青年基金资助项目(LR14E060001) 教育部博士点基金资助项目(20130101110097)
关键词 开放式燃烧 炭黑 微观结构 二恶英 多环芳烃 open-burning carbon black microstructure PCDD/Fs PAHs
  • 相关文献

参考文献1

二级参考文献6

  • 1姚素微 白世河 张卫国.水溶性接枝炭黑的制备方法[P].中国专利:CN 01141661.0.2002-05-01.
  • 2KATSUMI kamegawa,KEIKO Nishibo,MASAYA kadama, et al. Oxidative degradation of carbon blacks with nitric acidⅡ Formation of water-soluble polynuclear aromatic compounds[J]. Carbon,2002,40(9) :1447 - 1455.
  • 3BECK N V, MEECH S E, NORMAN P R, et al. Characterisation of surface oxides on carbon and their infleuence on dynamic adsorption [ J ]. Carbon, 2002,40(4) :531 -540.
  • 4季君晖.炭黑表面性能的表征[J].炭素,1999(4):8-12. 被引量:14
  • 5盛恩宏,周运友.碳黑的表面臭氧氧化[J].化学世界,2000,41(2):69-72. 被引量:6
  • 6魏彤,张友兰,王利军,白光君,魏淑杰.水性体系中炭黑分散的影响因素[J].涂料工业,2002,32(7):12-17. 被引量:10

共引文献16

同被引文献7

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部