摘要
In this work, graphene-modified epoxy-based anti-corrosion coatings were prepared and the influence of graphene on the anti-corrosion performance of the epoxy-based coatings was investigated with water contact angle test ,chemical solution immersion test, and electrochemical test. The water contact angle and chemical solution resistance of the epoxy-based coatings were improved with an increase in graphene content from 0 to 0.4%. These results prove that addition of graphene can significantly improve the hydrophobicity and impermeability of epoxy- based coatings. However, when the graphene content was increased to 0.5%, the performance of the epoxy-based coatings decreased because of graphene aggregation. Tafel polarization results show that graphene addition can significantly reduce the corrosion current density and corrosion potential of epoxy-based coatings, which enhance their anti-corrosion performance.
In this work, graphene-modified epoxy-based anti-corrosion coatings were prepared and the influence of graphene on the anti-corrosion performance of the epoxy-based coatings was investigated with water contact angle test ,chemical solution immersion test, and electrochemical test. The water contact angle and chemical solution resistance of the epoxy-based coatings were improved with an increase in graphene content from 0 to 0.4%. These results prove that addition of graphene can significantly improve the hydrophobicity and impermeability of epoxy- based coatings. However, when the graphene content was increased to 0.5%, the performance of the epoxy-based coatings decreased because of graphene aggregation. Tafel polarization results show that graphene addition can significantly reduce the corrosion current density and corrosion potential of epoxy-based coatings, which enhance their anti-corrosion performance.