为了提高纳米TiO_2对太阳光的利用率和实现光催化剂的回收再利用,采用溶胶-凝胶法将上转换荧光材料与纳米TiO_2复合,通过负载于活性炭纤维(ACF)表面制备了Pr3+:Y2SiO5/TiO_2/ACF复合材料。运用XRD、FT-IR、SEM、FS、UV-vis DRS等对材料的结构及性能进行了综合表征,并以亚甲基蓝为模拟污染物评价复合材料的可见光催化活性,考察了材料制备过程中煅烧温度、负载次数等制备条件对复合材料可见光下催化性能的影响。结果表明,在浸渍2次、800℃煅烧的制备条件下,复合材料中TiO_2为锐钛矿相(占34.1%)与金红石相(占65.9%)的混合相,亚甲基蓝(15 mg·L-1)12 h内去除率高达93.8%,反应符合拟一级动力学,反应速率常数为0.2471 h-1,回收再生利用4次后去除率仍保持在75%以上。
In order to improve sunlight utilization as well as to recycle and reuse photocatalyst of titanium dioxide, Pr3+:Y2SiO5/TiO2/ACF composites were prepared by sol-gel technique of anchoring upconversion fluorescent material and nano-titanium dioxide on activated carbon fiber(ACF). Structures and properties of the Pr3+:Y2SiO5/TiO2/ACF composites were characterized by XRD, FT-IR, SEM, FS, and UV-vis DRS. Photocatalytic activity of the composites in the visible light region was evaluated with methylene blue solution as model pollutant and studied the effect of fabrication conditions such as calcination temperature and number of coating layers. The experimental results showed that TiO2 in Pr3+:Y2SiO5/TiO2/ACF composite contained both anatase(34.1%) and rutile(65.9%) when prepared by double coating and 800 ℃ calcination. This composite had the highest visible-light photocatalytic activity which degraded methylene blue(15 mg·L-1) high as 93.8% in 12 h. The photodegradation followed pseudo first order kinetics with reaction rate constant is 0.2471 h-1. Pr3+:Y2SiO5/TiO2/ACF composite remained degradation rate above 75% after recycled and regenerated for use four times.
出处
《化工学报》
EI
CAS
CSCD
北大核心
2016年第11期4885-4891,共7页
CIESC Journal
基金
江苏省环境净化材料工程技术研究中心开放基金项目(KFK1504)
江苏省产学研前瞻性联合研究项目(BY2016004-02)
江苏高校优势学科建设工程资助项目(PAPD)~~
关键词
上转换
纳米TIO2
复合材料
吸附
降解
再生
upconversion
nano-titanium dioxide
composites
adsorption
degradation
regeneration