摘要
主要采用金相及SEM分析方法,对20Cr2Ni4A锻圆表面裂纹性质及产生原因进行了分析,结果表明锻圆表面裂纹是由于原材料存在表面夹杂/渣引起的。
The properties and the cause of the surface crack of 20Cr2Ni4A forging are analyzed by means of metallographic analysis and SEM analysis.The results show that the surface crack is caused by the inclusion on the surface of the raw material.
出处
《山西冶金》
CAS
2016年第5期33-34,共2页
Shanxi Metallurgy
关键词
钢锭
锻造
纵向裂纹
ingot
forging
longitudinal crack