Aiming to develop materials for construction of the set-up and electrode of high-temperature molten salt reactors, the effect of Al and Y on the high-temperature oxidation behavior of Ni-11Fe-10Cu at 750 and 950 °C in air were investigated. The oxidation kinetics of Ni-11Fe-10Cu alloy followed parabolic law at 750 °C without spallation and linear law at 950 °C with severe spallation, while that of Ni-11Fe-10Cu-6Al-3Y alloy followed parabolic law at 750 and 950 °C without spallation. The parabolic rate constant （kp） of Ni-11Fe-10Cu was smaller than that of Ni-11Fe-10Cu-6Al-3Y at 750 °C. The oxide scale formed on Ni-11Fe-10Cu at 750 °C was composed of a CuO outer layer, a NiFe2O4 middle layer and a NiO inner layer. The oxide scale formed on Ni-11Fe-10Cu-6Al-3Y at 750 °C was also composed of the similar triplex layers in addition to an internal oxidation zone containing Al, Ni and Cu oxide and the microstructure of the scale changed with increasing temperature. Although the doping Al and Y could improve the adherence of oxide scale, it could aggravate the extent of internal oxidation. Based on the combination of X-ray diffraction （XRD）, scanning electron mi-croscopy/energy dispersive spectroscopy （SEM/EDX） analysis, the microstructure and growth mechanism of the multi-layer oxide scale was studied and the effect of doping Al and Y on the oxidation behavior of Ni-11Fe-10Cu alloy was also discussed.
Aiming to develop materials for construction of the set-up and electrode of high-temperature molten salt reactors, the effect of Al and Y on the high-temperature oxidation behavior of Ni-11Fe-10Cu at 750 and 950 °C in air were investigated. The oxidation kinetics of Ni-11Fe-10Cu alloy followed parabolic law at 750 °C without spallation and linear law at 950 °C with severe spallation, while that of Ni-11Fe-10Cu-6Al-3Y alloy followed parabolic law at 750 and 950 °C without spallation. The parabolic rate constant （kp） of Ni-11Fe-10Cu was smaller than that of Ni-11Fe-10Cu-6Al-3Y at 750 °C. The oxide scale formed on Ni-11Fe-10Cu at 750 °C was composed of a CuO outer layer, a NiFe2O4 middle layer and a NiO inner layer. The oxide scale formed on Ni-11Fe-10Cu-6Al-3Y at 750 °C was also composed of the similar triplex layers in addition to an internal oxidation zone containing Al, Ni and Cu oxide and the microstructure of the scale changed with increasing temperature. Although the doping Al and Y could improve the adherence of oxide scale, it could aggravate the extent of internal oxidation. Based on the combination of X-ray diffraction （XRD）, scanning electron mi-croscopy/energy dispersive spectroscopy （SEM/EDX） analysis, the microstructure and growth mechanism of the multi-layer oxide scale was studied and the effect of doping Al and Y on the oxidation behavior of Ni-11Fe-10Cu alloy was also discussed.
基金
supported by the National Natural Science Foundation of China(51325102)
the International Science and Technology Cooperation Program of Ministry of Science and Technology(2015DFA90750)