EVA改性砂浆早龄期收缩应力/应变规律 被引量:7

Shrinkage Stress-Strain Evolution of Mortars Modified by EVA Polymer at Early Age
下载PDF
导出
摘要 采用自行设计的试验装置对可再分散醋酸乙烯-乙烯共聚物乳胶粉改性水泥砂浆(EVA改性砂浆)早龄期收缩应力/应变变化规律进行了初步研究,用X射线衍射对其水化产物钙矾石(AFt)、氢氧化钙(CH)和水化铝酸钙(C_4AH_(13))进行了表征,分析了收缩应力、应变变化与EVA掺量(质量分数)、水化产物的关系.结果表明:EVA可使改性砂浆早龄期收缩应力的增长速率变缓、最大收缩应变减小,且EVA掺量为15%时效果最明显;EVA既能抑制C_4AH_(13)的生成和转化,也能抑制AFt和CH的生成,并延缓水泥砂浆水化进程;在水化3h内,EVA改性砂浆的收缩应力变化只受AFt生成量的影响,而其收缩应变变化同时受CH和AFt生成量的影响,且与CH的相关性更大. A setup of testing the shrinkage stress and strain for cement mortars was designed.The evolutions of the shrinkage stress and strain of the mortars modified by EVA polymer were studied.Meanwhile,the hydration products of AFt,Ca(OH)_2,C_4AH_(13) were characterized by X-ray diffraction,the effect of EVA polymer addition on hydration process of mortars at early age were analyzed.The relationship between the development of shrinkage stress-strain and EVA addition and the relationship between the hydration products of AFt,Ca(OH)_2 and EVA addition were discussed.The results show that the addition of EVA causes the growth of shrinkage stress of mortar to slow down in advance and the maximum shrinkage strain reduces,and the effect of 15% EVA content(by mass)is more significant.Addition of EVA polymer delays the early hydration process of cement and reduces shrinkage stress/strain through inhibiting the formation and transformation of C_4AH_(13),as well as the formation of AFt and Ca(OH)_2.The trend analysis indicates that the shrinkage stress development of mortar modified by EVA polymer is affected by the amount of AFt in cement paste only within 3h,but not directly related to Ca(OH)_2.The shrinkage strain development of mortar modified by EVA polymer was affected by the amount of Ca(OH)_2and AFt in cement paste,and more related to Ca(OH)_2at early age.
作者 刘斯凤 万亭亭 王培铭 LIUSifeng WAN Tingting WANG Peiming(Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, Tongji University, Shanghai 201804, China)
出处 《建筑材料学报》 EI CAS CSCD 北大核心 2016年第5期791-796,共6页 Journal of Building Materials
基金 国家重点基础研究发展计划(973计划)项目(2011CB013800) "十二五"国家科技支撑计划项目(2012BAJ20B02)
关键词 改性砂浆 醋酸乙烯-乙烯共聚物乳胶粉(EVA) 收缩应力/应变 水化产物 相关性 modified mortar vinyl acetate ethylene copolymer redispersible powder(EVA) shrinkage stress/strain hydration product relativity
  • 相关文献

参考文献1

二级参考文献13

  • 1梁乃兴.丁苯橡胶对水泥水化过程及水泥石微观结构的影响[J].硅酸盐学报,1994,22(4):340-346. 被引量:18
  • 2OHAMA Y. Polymer-based admixture [J]. Cem Concr Compos, 1998, 20(2 3): 189-212.
  • 3OHAMA Y. Principle of latex modification and some typical properties of latex-modified mortars and concretes [J]. ACI Mater J, 1987, 84: 511-518.
  • 4SAKAI E, SUGITA J. Composite mechanism of polymer modified cement [J]. Cem Concr Res, 1995, 25(1): 127-135.
  • 5AFRIDI Mule, OHAMA Y, DEMURA K, et al. Development of polymer films by the coalescence of polymer particles in powdered and aqueous polymer-modified mortars [J]. Cem Concr Res, 2003, 33: 1 715-1 721.
  • 6BEELDENS A, MONTENY J, VINCKE W, et al. Resistance to sulphuric acid corrosion of polymer-modified mortars [J]. Cem Concr Compos, 2001, 23: 47-56.
  • 7SCHULZE J. Influence of water-cement ration and cement content on the properties of polymer-modified mortars [J]. Cem Concr Res, 1999, 29(6): 909-915.
  • 8ZHONG S, CHEN Z. Properties of latex blends and its modified cement mortars [J]. Cem Concr Res, 2002, 32(10): 1 515-1 524.
  • 9MIRZA J, MIRZA M S, LAPOINTE R. Laboratory and field performante of polymer-modified cement-based repair mortars in cold climates [J]. Construe Build Mater, 2002, 16(6): 365-374.
  • 10WANG R, WANG P M, LI X G. Physical and mechanical properties of styrene-butadiene rubber emulsion modified cement mortars [J]. Cem Concr Res, 2005, 35(5): 900-906.

共引文献26

同被引文献83

引证文献7

二级引证文献54

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部