The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It is found that the tensile properties of a novel Al-Cu-Li alloy are sensitive to aging processes, which correspond to different microstructures. σ（Al_5Cu_6Mg_2） and T_1（Al_2CuLi） phases are the major precipitates for the alloy in T6 aging condition（165 ℃/60 h）. After duplex aging condition（150 ℃/24 h ＋ 180 ℃/12 h）, σ, θ＇（Al_2Cu） and T_1 phases are detected. Only the T_1 phases can be found in the T8 state alloy（6% pre-strain＋135 ℃/60 h）. The failure modes of alloy in T6 and duplex aging conditions are dimple-intergranular fracture, while typical quasi-cleavage fracture in T8 condition.
The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It is found that the tensile properties of a novel Al-Cu-Li alloy are sensitive to aging processes, which correspond to different microstructures. σ（Al_5Cu_6Mg_2） and T_1（Al_2CuLi） phases are the major precipitates for the alloy in T6 aging condition（165 ℃/60 h）. After duplex aging condition（150 ℃/24 h ＋ 180 ℃/12 h）, σ, θ＇（Al_2Cu） and T_1 phases are detected. Only the T_1 phases can be found in the T8 state alloy（6% pre-strain＋135 ℃/60 h）. The failure modes of alloy in T6 and duplex aging conditions are dimple-intergranular fracture, while typical quasi-cleavage fracture in T8 condition.
基金
the National High Technology Research and Development Program of China (Grant No.2013AA032401)