摘要
为探究芳纶针织物复合材料的力学性能,用电子织物强力机对平板硫化机制得的芳纶针织物复合材料进行拉伸、弯曲、压缩性能测试,结果表明:芳纶针织物增强复合材料为非脆性破坏;经硅烷偶联剂处理有效地提高了芳纶针织物增强复合材料的抗拉、抗弯、抗压强度;罗纹空气层组织的抗拉、抗弯及抗压性能优于满针罗纹组织。
To explore the mechanical properties of aramid fiber knitted fabric reinforced composite, using electronic fabrics strength machine to stretch the composite materials made by press vulcanize, the tensile property, bending property, compression performance are tested. The results show that the aramid fiber knitted fabric reinforced composite is non-brittle fracture; the tensile strength, bending strength and compressive strength of aramid fiber knitted fabric reinforced composite are improved effectively by treatment of silane coupling agent; the tensile property, bending property and compressive performance of composites with rib air layer organization are superior to full needle rib construction.aramid fiber, composite material, knitted fabric, mechanical property
作者
王彦杰
孟家光
张琳玫
张永锋
WANG Yan-jie MENG Jia-guang ZHANG Lin-mei ZHANG Yong-feng(Xi'an Polytechnic University,Xi'an 710048,Shaanxi Shaanxi Province Cooperative Innovational Center for Technical Textiles,Xi'an 710048,Shaanxi,China)
出处
《合成纤维》
CAS
2016年第10期11-14,共4页
Synthetic Fiber in China
基金
国家支撑计划项目(2012BAF13B03)
陕西省重点学科专项资金支助项目(2008169)
关键词
芳纶
复合材料
针织物
力学性能
aramid fiber
composite material
knitted fabric
mechanical property