电纺PAN纳米纤维的AFM形貌及晶区分布研究

AFM morphology and crystalline region distribution of polyacrylonitrile nanofibers prepared by electrospinning
下载PDF
导出
摘要 目前已有很多学者对聚丙烯腈(PAN)静电纺丝进行了研究,但对其工艺的研究存在不同看法,同时关于电纺PAN纤维有序结构分布的研究较少。针对以上,系统研究了较宽范围内静电纺丝参数对PAN纤维形貌和直径的影响。经过对比,喷丝液浓度对所制备PAN纤维直径影响最大,随着喷丝液浓度从6%(质量分数)升高至18%(质量分数),纤维平均直径由288nm增大至3 469nm。将超声刻蚀法、原子力显微镜(AFM)、扫描电子显微镜(SEM)结合X射线衍射技术(XRD)对电纺PAN纤维内部结构进行研究。结果表明,电纺PAN纤维表面存在相互平行的横向沟槽,其中凸起部分为相对有序区域,宽度约为40-190nm,凹陷部分为无序区域,宽度约为20-35nm。 There have been a lot of deep researches about the electrospinning of PAN so far.But the works show different viewpoint about the PAN electrospinning and there is few researches about the ordered structure distri-bution of electrospun PAN fibers.The effects of electrospinning parameters in a wider range on the morphology and diameters of polyacrylonitrile (PAN)fibers are studied in detail.The result shows that the solution concen-tration has the greatest effect on the fibers diameter.The fibers’diameter increases swiftly from 288 to 3 469 nm with the PAN concentration increasing from 6% to 18wt%.Ultrasonic etching method,atomic force microscope (AFM),scanning electron microscope (SEM)and X-ray diffraction (XRD)technology have been u-tilized to verify the nature structure of electrospun PAN fibers.The optimal ultrasonic etching conditions were explored.Combining all the results,it is deduced that there are many grooves arranging nearly perpendicular to the fiber axis on the surface of electrospun PAN fibers.The grooves are the amorphous regions (thickness:20-35 nm)and the bulges are the relative ordered regions (thickness:40-190 nm).
出处 《功能材料》 EI CAS CSCD 北大核心 2016年第6期86-92,共7页 Journal of Functional Materials
基金 国家重点基础研究发展计划(973计划)资助项目(2011CB605601) 山东省重点自然科学基金资助项目(ZR2014EZ001)
关键词 静电纺丝 纳米纤维 超声刻蚀 AFM electrospinning nanofibers ultrasonic etching AFM
  • 相关文献

参考文献1

二级参考文献10

  • 1郑展望,雷乐成,张珍,岑沛霖.非均相UV/Fe-Cu-Mn-Y/H_2O_2反应催化降解4BS染料废水[J].环境科学学报,2004,24(6):1032-1038. 被引量:39
  • 2董永春,何陆春,李春辉,张宝华,朱红星.活性染料的太阳光催化脱色降解[J].四川大学学报(工程科学版),2005,37(4):49-53. 被引量:18
  • 3赵超,姜利荣,黄应平.Fenton及Photo-Fenton非均相体系降解有机污染物的研究进展[J].分析科学学报,2007,23(3):355-360. 被引量:23
  • 4PARRA S, GUASAQUILLO I, ENEA O, et al. Abatement of an azo dye on structured C-Nafion/Fe-Ion surfaces by photo-fenton reactions leading to carboxylate intermediates with a remarkable biodegradability increase of the treated solution [ J]. Journal of Physical Chemistry B, 2003, 107: 7026 - 7035.
  • 5DHANANJEYAN M R, KIWI J, ALBERS P, et al. Photoassisted immobilized fenton degradation up to pH 8 of azo dye orange II mediated by Fe^3+/nation/glass fibers [J]. Helvetica Chemica Acta, 2001, 84:3433 - 3445.
  • 6TAO X, MAW. Efficient degradation of organic poUutants mediated by immobilized iron tetrasulfophthalocyanine under visible light irradiation [ J]. Chemical Communication, 2003, 3(1): 80-81.
  • 7ISHTCHENKO V V, HUDDERSMAN K D, VITKOVSKAYA R F. Production of a modified PAN fibrous catalyst and its optimisation towards the decomposition of hydrogen peroxide [J]. Applied Catalysis A, 2003, 242:123- 137.
  • 8ISHTCHENKO V V, VITKOVSKAYA R F, HUDDERSMAN K D. Investigation of the mechanical and physicochemical properties of a modified PAN fibrous catalyst [J]. Applied Catalysis A, 2003, 242:221 - 231.
  • 9FENG J, HU X, YUE P L, et al. Degradation of Azo-dye Orange II by a photoassisted fenton reaction using a novel composite of iron oxide and silicate nanopartieles as a catalyst [ J]. Industrial Engineering Chemistry Research, 2003,42 : 2058 - 2066.
  • 10董永春 韩振邦 董文静 等.海藻酸铁光催化剂的制备及其在酸性黑234降解反应中的应用.应用化学,2007,24:554-559.

共引文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部