改性光引发剂和优化光固化工艺制备低VOC涂料 被引量:3

Preparation of Low-VOC Coatings with Polyurethane Modified Photoinitiator and Optimized UV-Curing Technology
下载PDF
导出
摘要 为了降低光引发剂固化前后释放的味道,一方面通过多官能团的异氰酸酯预聚物对其进行改性,制备环保型光引发剂;另一方面,研究光引发剂在漆膜中的光解反应动力学,优化光固化工艺来减少漆膜的气味。通过正交试验优化低VOC紫外光固化涂料的配方为:25%的环氧丙烯酸树脂、43%的聚氨酯丙烯酸树脂、22%的二官能团活性稀释剂、7%的三官能团活性稀释剂、3%的改性光引发剂。优化的UV光固化涂装工艺参数为:膜厚50μm,UV灯管功率为1 k W,传送带速率为1 m/min。制备的涂料和漆膜几乎没有气味,漆膜的VOC排放为0.5%,且漆膜性能较佳,适用于环保木器UV涂料及其涂装。 In order to reduce the odor caused by photoinitiator released during the UV-cu- ring process, odorless photoinitiators were prepared by chemical modification with multifunctional isocyanate prepolymers containing OH groups. Then, the kinetics of these polyurethane modified photoinitiators in the UV-curing films were studied. The curing parameters were opti-mized in order to get odorless UV-cured films. The optimum formulation of odorless UV-cura- ble coatings was determined by the orthogonal test: 25% epoxy acrylic resin, 43% polyure- thane acrylate, 22% bifunctional reactive diluent, 7% trifunctional reactive diluent and 3% the modified photoinitiator. The optimum UV-curing parameters were obtained : 50μm of film thickness, 1 kw of UV-curing power and 1 meter per minute of UV-curing transmission speed. Both the UV-curable coatings and films were odorless. The films showed good performances and the VOC of film was 0. 5%, which were applicable to odorless wood UV-curing process.
出处 《涂料工业》 CAS CSCD 北大核心 2016年第12期29-35,共7页 Paint & Coatings Industry
关键词 低VOC涂料 UV固化 改性光引发剂 正交试验 odorless coatings UV - curable coatings modified photoinitiator orthogonal test
  • 相关文献

参考文献4

二级参考文献27

  • 1金玉杰,白晓春.用半衰期法验证蔗糖水解反应级数[J].兰州石化职业技术学院学报,2004,4(3):36-37. 被引量:2
  • 2粟智.浓度—时间比法确定反应级数和计算速率常数[J].计算机与应用化学,2005,22(3):235-238. 被引量:11
  • 3肖浦,吴刚强,史素青,聂俊.基于α-羟烷基苯酮(HAPK)可聚合大分子光引发剂的合成及其引发三丙二醇双丙烯酸酯(TPGDA)光聚合动力学的研究[J].感光科学与光化学,2006,24(3):204-210. 被引量:10
  • 4[1]Zhu S W,Shi W F.Flame retardance of UV cured epoxy acryhte blended with different states of phosphated methacrylate[J].Polym.Degrad.and Stab.,2003,82:435.
  • 5[3]Anseth K S,Newman S M,Bowman C N.Polymeric dental composites:properties and reaction behavior of multimethacrylate dental restorations[J].Adv.Polym.Sci.,1995,122:177-217.
  • 6[4]Arsu N,Davidson R S,Holman R.Factors affecting the photoyellowing which occurs during the photoinitiated polymerization of acrylates[J].J.Photoch.and Photobio.A,1995,87:169-175.
  • 7[5]BASF Aktiengesellachaft.Polyurethanes with covalendy bonded photoinitiator unita[P].US Patent,6031044,2000.
  • 8[6]Merck.Photoinitiator copolymer[P].EP:0341560,1989.
  • 9[7]Scherzer T,Decker U.Real-time FTIR-ATR spectroscopy to study the kinetics of ultrafast photopolymerization reactions induced by monochromatic UV light[J].Vibrational Spectroscopy,1999,19:385-398.
  • 10[8]Kerbonc'h P,Lebaudy P,Lecamp L,Bunel C.Numerical simulation to correlate photopolymerization kinetics monitoring by RT-NIR spectroscopy and photocalorimetry[J].Thermchimica Acta,2004,410:73-78.

共引文献23

同被引文献16

引证文献3

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部