减震胶套壳体的断裂原因分析 被引量:2

Analysis on Fracture Reasons of Shells of Damping Rubber Sleeves
下载PDF
导出
摘要 某厂生产的减震胶套在台架试验过程中,于壳体焊接部位发生脆性断裂。采用化学成分分析、断口分析、金相检验及焊条药皮水含量测试的方法,分析了减震胶套壳体断裂失效的原因。结果表明:壳体焊接部位断裂属于氢脆断裂;主要原因是焊接材料中的水含量过高,且焊接之前未对焊料进行烘干脱水处理;次要原因是焊接过程中壳体材料组织晶粒长大,增加了脆断的敏感性。 A batch of damping rubber sleeves produced by a factory fractured in welded part of shells in the process of bench test.Failure reasons of shells of damping rubber sleeves were analyzed by methods of chemical composition analysis,fracture analysis,metallographic examination and water content test of the electrode coating.The results show that:the fracture on welded shell belonged to hydrogen brittle fracture;the main reason of the fracture was that moisture content in the solders was excessively high,and the solders were directly used without drying and dewatering;the secondary reason was that the grains in the shells material grew in the welding process,which increased the sensitivity of the brittle fracture.
作者 钟奇鸣 李翔
出处 《理化检验(物理分册)》 CAS 2016年第11期825-827,共3页 Physical Testing and Chemical Analysis(Part A:Physical Testing)
关键词 减震胶套 壳体 断裂 氢脆 水含量 晶粒长大 damping rubber sleeve shell fracture hydrogen brittleness moisture content grain growth
  • 相关文献

参考文献4

二级参考文献17

共引文献62

同被引文献26

引证文献2

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部