The surface of SiO2 support was pretreated by C1-C4 normal alcohols before the impregnation of iridium and rhenium precursors.These catalysts were applied in high concentration glycerol aqueous solution hydrogenolysis.The catalysts prepared from the pretreated supports exhibited high catalytic activity because of the formation of more active sites from a high dispersion of iridium oxide and rhenium oxide.The catalysts with the support pretreated by 1-propanol showed the highest glycerol conversion of 59.5%.The supports and catalysts were characterized by FT-IR,nitrogen adsorption,TPR,XRD,TEM,H2-chemisorption and NH3-TPD.
甘油是生物柴油的副产物,将其转化为高附加值的化学品,能提高生物柴油产业的经济性.1,3-丙二醇是聚酯和聚氨酯的单体,也用于合成医药和用作有机合成中间体,甘油直接催化氢解反应制1,3-丙二醇极具发展潜力.另外,甘油是生物质转化的重要平台分子之一,与目标产物的分子结构相比较,生物质平台分子通常含有过多的含氧基团,尤其是多余的羟基,通过甘油氢解反应研究多羟基的选择性活化和脱除,可以加深对生物质脱氧规律的认识.因此,研究甘油氢解反应制1,3-丙二醇催化剂和工艺,不仅具有潜在的应用前景,而且具有重要理论价值.然而,目前的甘油氢解催化剂性能还不够高,我们希望通过一些表面改性的方法处理载体硅胶,从而改变金属前驱体与载体表面的作用.因此,本文使用C1–C4的正构醇处理硅胶载体,其负载的Ir-Re催化剂上甘油氢解反应转化率从42.7%提高到59.5%,仲羟基脱除收率从21.6%提高到28.3%.研究发现,当处理载体所用正构醇的碳数从1增加到3时,对应催化剂上甘油转化率逐渐增加至最高;但当使用更正丁醇时,对应催化剂上甘油转化率下降.为了探究催化剂活性改变的原因,我们首先采用红外光谱(FT-IR)和氮气物理吸附确定烷氧基基团嫁接到硅胶载体上.程序升温还原结果发现,预处理载体相应的催化剂开始还原温度降低,表明在这些催化剂上形成了颗粒尺寸较小的Ir粒子.X-射线衍射分析发现,在新鲜的和使用后的催化剂上均未检测出Re物种的衍射峰,说明Re高度分散于催化剂表面.吸附吡啶的FT-IR结果表明,未处理和丙醇预处理硅胶负载的催化剂上均没有强酸位,它们的B/L酸比值相近,约为3.3.催化剂的吸附COFT-IR结果表明,CO线性吸附于Ir/SiO_2催化剂上的主要吸收峰位置在2084 cm^(–1);而Re的加入使得该吸收峰红移,表明Ir和ReO_x物种之间存在相互作用.透射电镜(TEM)、H_2-程序升温脱附和NH_3-程序升温脱附结果发现,醇预处理催化剂上具有更多的Ir-ReO_x界面,而界面位点的数量与甘油转化率大小一致,表明Ir-ReO_x位点可能就是甘油氢解的活性中心.反应后催化剂的TEM结果表明,醇预处理催化剂上的Ir颗粒要小于未处理催化剂的,其中丙醇预处理硅胶负载的催化剂上Ir粒径最小.这是由于醇处理催化剂上存在很多孤立的Si–OH,它们与金属前驱体相互作用有利于形成较小的金属颗粒.这些孤立的Si-OH则是由于表面烷氧基基团的隔离作用所形成的.当处理载体所用正构醇的碳数从1增加到3时,烷氧基的碳链变长,分隔作用越好,阻止金属前驱体聚集的程度越强,因而Ir物种和Re物种的分散度增加.但是当处理醇的碳数增加到4时,形成的表面烷氧基基团可能阻止了Re物种和Ir物种间相互作用,从而使得Ir和Re物种的分散度均降低,相应催化剂活性随之降低.
基金
supported by the National Natural Science Foundation of China(21403217)~~