CuNiCoBe与CuCrZr合金电极的点焊性能比较及其失效分析 被引量:1

Comparison of spot welding performance and failure analysis of CuNiCoBe and CuCrZr electrodes
下载PDF
导出
摘要 文中对比研究了CuNiCoBe合金与CuCrZr合金电极点焊镀锌钢板的性能,并利用超景深显微镜,光谱仪、XRD等分析测试手段研究了电极表面的剥落、端部塑性变形的程度及表面合金层的成分和物相等,分析了电极失效机理.结果表明,在相同的点焊工艺参数下,CuNiCoBe电极点焊寿命达到3 500点,为CuCrZr电极寿命1 500点的2.3倍.CuCrZr电极寿命低于CuNiCoBe电极的原因在于CuCrZr合金强度硬度低,易形成剥落孔洞、塑性变形大,电极端部尺寸增大明显.表面合金层的成分和产物和CuNiCoBe电极的不尽相同. The spot-welding performances of galvanized steel were compared between and CuNiCoBe and CuCrZr electrodes.The peeling of electrode surface,the degree of plastic deformation of the end portion and the composition and phases of the surface layer were studied by means of super depth of field microscope,Spectrometer,XRD and so on,and the failure mechanism of electrodes were analyzed.The results had shown that at the same parameters,the life of CuNiCoBe electrode is 3500 points,which is 1.3 times higher than that of CuCrZr electrode,which mainly caused by the low intensity and hardness of CuCrZr alloy,large possibility to form peeling holes,the large size of plastic deformation and apparent increase of size of electrode tip.The compositions and products of surface layer of CuCrZr electrode is not the same as that of CuNiCoBe electrode.
出处 《焊接学报》 EI CAS CSCD 北大核心 2016年第12期101-106,共6页 Transactions of The China Welding Institution
基金 江苏高校优势学科建设工程资助项目
关键词 铜镍钴铍合金 铬锆铜合金 镀锌钢板 点焊寿命 CuNiCoBe alloy CuCrZr alloy galvanized steel life of spot-welding
  • 相关文献

参考文献9

二级参考文献59

共引文献82

同被引文献6

引证文献1

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部