摘要
采用溶胶-凝胶法制备了不同K^+掺杂量的纳米TiO_2粉体,利用差热-热重、X衍射仪研究了不同煅烧温度、不同煅烧时间下K^+掺杂量对TiO_2凝胶相变过程的影响。研究结果表明,提高煅烧温度、延长煅烧时间可有效促进锐钛矿(Anatase)向金红石(Rutile)(A-R)的转变,K+掺杂抑制了锐钛矿向金红石的转变。
TiO_2 nanopowders with different K^＋ doping amounts were prepared by the sol-gel method.The effect of K^＋ doping on the phase transformation of TiO_2 gels was investigated under different calcination temperature and time by TG-DTA,XRD technique.The results showed that the increase of calcination temperature and calcination time promoted TiO_2 phase transformation from anatase to rutile.In addition,K^＋ doping decreased the transformation from anatase to rutile.
出处
《化工新型材料》
CAS
CSCD
北大核心
2017年第1期202-204,共3页
New Chemical Materials