摘要
采用熔融-晶化法制备了Tb^(3+)掺杂的CaMoO_4为主晶相的透明钼酸盐玻璃陶瓷。利用DSC、XRD、SEM确定了该体系玻璃样品的最佳热处理制度:715℃保温2.5 h;随着热处理时间的增加,玻璃陶瓷中的晶粒尺寸逐渐变大;利用UV-Vis-NIR得到样品玻璃陶瓷在可见光区的透过率可达80%;并利用荧光光谱讨论了在相同热处理条件下,不同Tb^(3+)掺杂浓度对玻璃陶瓷样品发光性能的影响,研究表明Tb^(3+)掺杂浓度为7.0mol%时样品的荧光强度最大。
Tb^3+ doped transparent molybdate glass ceramics containing CaMoO4 were successful fabricated by melt-quenching technique. The optimal heat-treated system for the glass sample was determined by DSC,XRD and SEM( 715 ℃ for 2. 5 h). The grain size of the glass ceramics gradually increased with the increasing of heat treatment time. The UV-Vis-NIR spectra indicated that the sample transparency was approximately up to 80% in visible light range. The effect of different Tb^3+ doping concentration on the luminescence properties of the glass ceramics under the condition of the same heat treatment by fluorescence spectrum. The experimental result indicated that the Tb^3+ doping concentration was 7. 0mol%,the sample has the maximum fluorescence intensity.
出处
《硅酸盐通报》
CAS
CSCD
北大核心
2017年第1期306-310,共5页
Bulletin of the Chinese Ceramic Society
基金
国家高技术研究发展计划(863计划)(2011AA030204)
吉林省科技厅重点项目(20150204051GX
20160204027GX)