含不同类型氧化锌丁腈橡胶的干摩擦行为研究

Study on Tribological behavior of Nitrile-butadiene Rubber Containing Different Kinds of Zinc Oxide under Dry Sliding

制备普通氧化锌与纳米氧化锌填充的丁腈橡胶(NBR),分析氧化锌类型对NBR材料特性及物理机械性能的影响。在MPV-600型磨粒磨损试验机上研究氧化锌类型对NBR摩擦磨损性能的影响,采用扫描电镜对磨损表面形貌进行观察,分析其磨损机制。结果表明:与普通氧化锌硫化胶相比,纳米氧化锌可使NBR的拉伸强度、定伸应力进一步提高;加入纳米氧化锌的NBR的最大转矩提高,焦烧时间与正硫化时间都较普通氧化锌的缩短;添加纳米氧化锌的NBR的耐摩擦磨损性能优异,这主要归因于其具有更大的交联密度与较高的体系硬度。添加纳米氧化锌的NBR的磨损机制为磨料磨损和少量的黏着磨损,而添加普通氧化锌的NBR的磨损机制为磨料磨损和严重的黏着磨损。

Nitrile-butadiene rubber （NBR） materials filled by conventional ZnO （c-ZnO） and nano-ZnO （n-ZnO） were prepared, and the material properties and physical and mechanical performances of Nitrile-butadiene rubber （NBR） containing different kinds of Zinc Oxide （ZnO） were analyzed.The influences on tribological properties of NBR by types of ZnO were studied by using MPV-600 abrasive wear tester, the morphology of worn surface was measured by scanning elec- tron microscopy （SEM） ,and the wear mechanism was analyzed.The results indicate that, compared with NBR containing c- ZnO, the n-ZnO can further improve the tensile strength and tensile stress of NBR.Tlie maximum torque of NBR containing n-ZnO is higher than that of NBR containing c-ZnO, and the scorch time and optimum cure time of NBR containing n-ZnO are both shortened.The NBR containing n-ZnO exhibits the more outstanding wear resistance, which is mainly due to its greater crosslinking density and higher systematic hardness.The wear mechanism of NBR containing n-ZnO is abrasive wear and little adhesive wear ,while that of NBR containing c-ZnO is abrasive wear and serious adhesive wear.