硅烷偶联剂改性芳纶工艺研究 被引量:6

Study on Modification of Aramid Fiber with Silane Coupling Agent
下载PDF
导出
摘要 采用KH550硅烷偶联剂处理芳纶,将处理温度、时间、硅烷偶联剂的质量分数作为3个因素进行分析,通过单因素分析法确定每个因素对处理前后芳纶与树脂的界面剪切强度的影响,结合扫描电镜观察处理前后纤维的表面结构变化,得到最佳处理的工艺为:处理时间9 h、温度45℃、硅烷偶联剂的质量分数为25%。 Aramid fiber was modified with silane coupling agent KH550. The treatment temperature, time, concentration of the silane coupling agent were analyzed as three factors. Each of these factors was determined by the single factor analysis before and after treatment, combined with the influence of the interfacial shear strength of aramid fiber and resin, fiber surface structure changes observed before and after treatment with scanning electron microscope, the optimal treatment processes were: time 9 h, temperature 45 ℃, concentration of silane coupling agent 25%.
出处 《合成纤维》 CAS 2017年第1期30-33,共4页 Synthetic Fiber in China
基金 国家支撑计划项目(2012BAF13B03) 陕西省重点学科专项资金支助项目(2008169) 陕西省产业用纺织品协同创新中心科研资助项目(2015ZX-06)
关键词 芳纶 硅烷偶联剂 界面剪切强度 aramid fiber silane coupling agent interfacial shear strength
  • 相关文献

参考文献6

二级参考文献104

共引文献43

同被引文献686

引证文献6

二级引证文献26

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部