摘要
通过现场工况调研、化学成分分析、组织形貌观察和电化学测试等手段分析了耐酸碟阀腐蚀的原因。结果表明:局部腐蚀穿孔和腐蚀坑主要是由铸件缺陷所引起的,而阳极保护系统引起的电解腐蚀是导致严重均匀腐蚀的主要原因。
The corrosion failure of acid resistant butterfly valve was analyzed by means of in-situ work condition investigation, chemical composition analysis, microstructure and corrosion morphology observation as well as electrochemical testing. The results show that the localized corrosion perforation and pits were due to casting defects. The main reason for heavy general corrosion was electrolytic corrosion because of anodic protection system.
出处
《腐蚀与防护》
CAS
北大核心
2017年第2期155-159,共5页
Corrosion & Protection
关键词
碟阀
腐蚀
电解腐蚀
失效分析
butterfly valve
corrosion
electrolytic corrosion
failure analysis