摘要
Cast-mono crystalline silicon wafers contain crystallographic defects, which can severely impact the electrical performance of solar cells. This paper demon- strates that applying hydrogenation processes at moderate temperatures to finished screen print cells can passivate dislocation clusters within the cast-mono crystalline silicon wafers far better than the hydrogenation received during standard commercial firing conditions. Efficiency enhancements of up to 2% absolute are demonstrated on wafers with high dislocation densities. The impact of illumination to manipulate the charge state of hydrogen during annealing is investigated and found to not be significant on the wafers used in this study. This finding is contrary to a previous study on similar wafers that concluded increased H or H0 from laser illumination was responsible for the further passivation of positively charged dangling bonds within the dislocation clusters.
Cast-mono crystalline silicon wafers contain crystallographic defects, which can severely impact the electrical performance of solar cells. This paper demon- strates that applying hydrogenation processes at moderate temperatures to finished screen print cells can passivate dislocation clusters within the cast-mono crystalline silicon wafers far better than the hydrogenation received during standard commercial firing conditions. Efficiency enhancements of up to 2% absolute are demonstrated on wafers with high dislocation densities. The impact of illumination to manipulate the charge state of hydrogen during annealing is investigated and found to not be significant on the wafers used in this study. This finding is contrary to a previous study on similar wafers that concluded increased H or H0 from laser illumination was responsible for the further passivation of positively charged dangling bonds within the dislocation clusters.