Synthesis of malachite@clay nanocomposite was successfully carried out for the removal of cationic（Methylene Blue,MB） and anionic dyes（Congo Red,CR） from synthetic wastewater.Nanocomposite was characterized by TEM,SEM,FT-IR,EDS analysis and zeta potential.TEM analysis indicated that the particle diameter of nanocomposite was in the range of 14 to23 nm.Various important parameters viz.contact time,concentration of dyes,nanocomposite dosage,temperature and solution pH were optimized to achieve maximum adsorption capacity.In the case of MB,removal decreased from 99.82%to 93.67%while for CR,removal decreased from 88.55%to 75.69%on increasing dye concentration from 100 to 450 mg/L.pH study confirmed the higher removal of CR in acidic range while MB removal was higher in alkaline range.Kinetic study revealed the applicability of pseudo-second-order model for the adsorption of both dyes.Negative values of AG0 for both systems suggested the feasibility of dye removal and support for spontaneous adsorption of CR and MB on nanocomposite.Nanocomposite showed 277.77 and 238.09 mg/g Langmuir adsorption capacity for MB and CR respectively.Desorption of dyes from the dye loaded nanocomposite was easily carried out with acetone.The results indicate that the prepared malachite@clay nanocomposite is an efficient adsorbent with high adsorption capacity for the aforementioned dyes.
Synthesis of malachite@clay nanocomposite was successfully carried out for the removal of cationic（Methylene Blue,MB） and anionic dyes（Congo Red,CR） from synthetic wastewater.Nanocomposite was characterized by TEM,SEM,FT-IR,EDS analysis and zeta potential.TEM analysis indicated that the particle diameter of nanocomposite was in the range of 14 to23 nm.Various important parameters viz.contact time,concentration of dyes,nanocomposite dosage,temperature and solution pH were optimized to achieve maximum adsorption capacity.In the case of MB,removal decreased from 99.82%to 93.67%while for CR,removal decreased from 88.55%to 75.69%on increasing dye concentration from 100 to 450 mg/L.pH study confirmed the higher removal of CR in acidic range while MB removal was higher in alkaline range.Kinetic study revealed the applicability of pseudo-second-order model for the adsorption of both dyes.Negative values of AG0 for both systems suggested the feasibility of dye removal and support for spontaneous adsorption of CR and MB on nanocomposite.Nanocomposite showed 277.77 and 238.09 mg/g Langmuir adsorption capacity for MB and CR respectively.Desorption of dyes from the dye loaded nanocomposite was easily carried out with acetone.The results indicate that the prepared malachite@clay nanocomposite is an efficient adsorbent with high adsorption capacity for the aforementioned dyes.
基金
financial supports from the Regional Council of South-Savo and the City of Mikkeli,Finland