摘要
通过溶胶-凝胶制备双钙钛矿PrBaCo_2O_(5+δ)(PBCO)中温固体氧化物燃料电池阴极材料,研究结果表明:PrBaCo_2O_(5+δ)为四方结构.在100~850℃内,PBCO样品为金属导电机制.交流阻抗谱的测试结果表明:PrBaCo_2O_(5+δ)电极在800℃时的极化电阻为0.034 8Ω·cm^2.采用La_(0.9)Sr_(0.1)Ga_(0.8)Mg_(0.2)O_(3-δ)(LSGM)电解质为支撑体的单电池在800℃时的功率密度达到558.7 m W/cm2.
Double-perovskite PrBaCo_2O_(5+δ)(PBCO) is synthesized by the sel-gel complex method,and investigated as a novel cathode material for intermediate-temperature solid oxide fuel cells(IT-SOFCs).PBCO shows a tetragonal structure.The electrical conductivities of PBCO sample occurs a metal conductive mechanism between100 oC and 850 oC.The lowest polarization resistance of 0.034 8 Ω·cm-2is achieved at 800 ℃.The power densities of a single cell with PBCO cathode with La_(0.9)Sr_(0.1)Ga_(0.8)Mg_(0.2)O_(3-δ)(LSGM) electrolyte is 558.7 m W/cm2 at 800 ℃.
作者
梁磊
陈红
Liang Lei Chen Hong(Physics College of Beihua University ,Jilin 132013, China)
出处
《北华大学学报(自然科学版)》
CAS
2017年第2期160-163,共4页
Journal of Beihua University(Natural Science)
基金
吉林省教育厅科学技术研究项目(201654)
关键词
固体氧化物燃料电池
阴极
双钙钛矿
电化学性能
solid oxide fuel cell
cathode
double perovskite
electrochemical performance