Mechanistic Insights into the Shear Effects on Isotactic Polypropylene Crystallization Containingβ-Nucleating Agent

The crystalline structures and crystallization behaviors of iPP containing β nucleation agent TMB-5 （iPP/TMB-5） were investigated by synchrotron radiation wide angel X-ray diffraction （SR-WAXD）, differential scanning calorimeter （DSC） and polarized light microscope （PLM）. It was found that α-crystallization lagged behind β-crystallization at normal temperatures, but the discrepancy reduced with increasing temperature. TMB-5 could not induce β-iPP when the nucleation agent is wrapped up with α-crystal that crystallized at high temperatures. The polymorphic composition of iPP/TMB-5 was susceptible to the introductory moment of shear. New crystallization process of β-nucleated iPP was proposed to understand the experimental phenomena which could not be explained by those reported in the literature. It was supposed that polymer crystallization initiated from mesophase, and the formations of iPP crystals involved the organization of helical conformation ordering within rnesophase. It was proposed that the iPP melt contained mesophases with stereocomplex-type ordering of right-handed and left-handed helical chains which could be disturbed by shear or TMB-5, leading to different polymorphic structures.