摘要
本文以含锌53.35%、含铁13.51%及铁酸锌13.97%的锌焙砂为原料,在对锌焙砂粒度分析、X-荧光多元素半定量分析、XRD分析及锌铁物相分析基础上,采用硫酸做浸出剂,研究始酸浓度、液固比、搅拌速度、浸出温度、浸出时间等因素对浸出渣物性的影响。结果表明,获取高含量ZnFe_2O_4浸出产品的试验条件为:始酸浓度100 g/L、液固比8∶1、搅拌速度400 r/min、浸出温度75℃、浸出时间120 min。
In this paper,zinc calcine with 53. 35%Zn,13. 51%Fe and 13. 97%zinc ferrite as raw materials was studied by the analysis of granularity,X-ray fluorescence multi-element semi-quantitative,XRD and zinc iron phase.The influence of sulfuric acid concentration,solid-liquid ratio,stirring speed,leaching temperature and leaching time was studied on leaching residue properties.The results show that the leaching conditions obtained high content ZnFe2O4 is initial acid concentration100 g/L,liquid-solid ratio 8 ∶ 1,stirring speed 400 rpm,leaching temperature 75℃ and leaching time 120 min.
作者
杨金林
徐明
罗美秀
马少健
刘平
Yang jinlin Xu Ming Luo Meixiu Ma Shaojian Liu Ping(School of Resources and Metallurgy, Guangxi University, Nanning, Guangxi, China GuiLin University of Technoli3gy at Nanning, Nanning, Guangxi, China)
出处
《矿产综合利用》
CAS
北大核心
2017年第1期97-101,共5页
Multipurpose Utilization of Mineral Resources
基金
广西大学广西有色金属及特色材料加工重点实验室开放基金(GXKFJ16-01)
国家自然科学基金(51364003)
广西博士后专项资金
广西高校矿物工程重点实验室资助项目
关键词
锌焙砂
硫酸浸出
铁酸锌
Zinc calcine
Sulfuric acid leaching
Zinc ferrite