摘要
Hierarchically porous anatase TiO_2 microspheres composited with carbonaceous species(TCS) have been successfully fabricated by a one-step template-free solvothermal method,combined with subsequent low temperature dried process.In this configuration,the TCS microspheres are constructed by the interconnected porous nanosheets,which are further assembled with abundant nanoparticles and carbonaceous species.Such composite microspheres possess a large specific surface area of 337 m^2g^(–1),uniform mesopores of 3.37 nm and high total pore volumes of 0.275 cm3g–1.The materials exhibit the enhanced photocatalytic properties and stability for degradation of rhodamine B(Rh B) under visible-light irradiation.The enhanced photocatalytic degradation performance may be ascribed to their abundant porous structure,large specific surface area and the unique assist-function of the carbonaceous species.
Hierarchically porous anatase Ti02 microspheres composited with carbonaceous species (TCS) have been successfully fabricated by a one-step template-free solvothermal method, combined with subsequent low temperature dried process. In this configuration, the TCS microspheres are constructed by the intercon- nected porous nanosheets, which are further assembled with abundant nanoparticles and carbonaceous species. Such composite microspheres possess a large specific surface area of 337 m2 g-l, uniform mesopores of 3.37 nm and high total pore volumes of 0.275 cm3 g-1. The materials exhibit the enhanced photocatalytic properties and stability for degradation of rhodamine B (RhB) under visible-light irradiation. The enhanced photocatalytic degradation performance may be ascribed to their abundant porous structure, large specific surface area and the unique assist-function of the carbonaceous species.
基金
financially supported by the National Natural Science Foundation of China(Nos.61271126,21547012 and 21305033)
the Program for Innovative Research Team in University(No.IRT-1237)
the Program for Science and Technology Project of Heilongjiang province(Nos.B201414 and B2015008)
the Heilongjiang Educational Department(No.2013TD002,2011CJHB006,12531506)
the Youth Foundation of Harbin(No.2015QQQXJ047)