采用硬度与电导率测试、拉伸试验、晶间腐蚀和剥落腐蚀试验并借助X射线衍射(XRD)、扫描电镜(SEM)、电子背散射衍射(EBSD)等方法,研究了预回复退火对Al-11.5Zn-3.5Mg-2.3Cu-0.24Zr铝合金挤压材固溶-T652处理组织与性能的影响。结果表明:与未经预回复退火相比,预回复退火可有效抑制合金的再结晶,细化晶粒尺寸,降低平均晶界角度,显著提高低角度晶界百分比;预回复退火能够保持同等抗拉强度的情况下,提高该合金的屈服强度和抗腐蚀性能;位错强化和低角度晶界强化是合金屈服强度提高的主要因素。
Effect of pre-recovery solid solution-T652 treatment and solid solution-T652 treatment on microstructure and properties of Al-11.5Zn-3.5Mg-2.3Cu-0.24Zr-0.0025 Sr aluminum alloy extrusion were studied by micro-hardness tester and electrical conductivity test, tensile test, intergranular and exfoliation corrosion experiment, scanning electron microscope（SEM） and el ectron back-scattered diffraction（EBSD）. The results show that pre-recovery-annealing treatment can restrain recrystallization effectively, refine the grain size, reduce the average angle of grain boundaries, and increase the percentage of low angle grain boundaries significantly. Pre-recovery-annealing can improve the yield strength and the corrosion resistance performance, and maintain the same tensile strength. The increase of the yield strength is attributed to dislocation strengthening and low angel g rain boundaries strengthening.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2017年第3期796-801,共6页
Rare Metal Materials and Engineering
基金
江苏省工业科技支撑计划项目(BE2008118)
江苏大学优秀青年学术骨干培育专项基金(1211110001)
江苏省高校研究生科研创新计划项目(CXLX110563)
江苏高校优势学科建设工程项目
关键词
预回复退火
挤压材
拉伸性能
腐蚀性能
pre-recovery-annealing
extrusion
tensile properties
corrosion performance