氯盐侵蚀是引起钢筋锈蚀的主要原因,直接影响混凝土结构耐久性。本文基于氯离子侵蚀混凝土机理,讨论了氯盐腐蚀环境混凝土寿命预测模型的进展及主要钢筋腐蚀防护措施,简析了几种措施的优缺点。
Chloride corrosion is the main cause of corrosion of steel bars,which directly affects the durability of concrete structures.Based on the mechanism of chloride ion erosion,this paper discusses the progress of the concrete life prediction model in the chloride salt corrosion environment and the main protection measures to steel corrosion,analyzing the advantages and disadvantages of these measures.
出处
《科技视界》
2017年第2期129-129,96,共2页
Science & Technology Vision
关键词
氯盐侵蚀
钢筋锈蚀
混凝土结构
Chloride corrosion
Steel corrosion
Concrete structures