摘要
In this paper, the process of photocatalytic reduction of hexavalent chromium was investigated over Ti3＋- modified TiO2 photocatalysts. The Ti3＋ surface defects were repaired by annealing as-prepared sample at different temperatures to control the amount of Ti3＋ sites. The samples were characterized by SEM, XRD, BET, UV-Vis absorption, EPR and XPS. The results showed Ti3＋ defects were successfully doped in TiO2. The surface selective adsorption of hexavalent chromium [Cr2072 （Cr（VI））] and the desorption of trivalent chromium [Cr3＋ （Cr（III））] were investigated during the process ofphotocatalytic reduction positive charges due to more Ti3＋ defects on the surface show a Accordingly, the surface positive reduction of Cr（VI）. charges controlled by the Ti3＋ Zeta potential results presented that the increased significant improvement for adsorption of Cr（VI）. defects play important roles in the photocatalytic
In this paper, the process of photocatalytic reduction of hexavalent chromium was investigated over Ti3＋- modified TiO2 photocatalysts. The Ti3＋ surface defects were repaired by annealing as-prepared sample at different temperatures to control the amount of Ti3＋ sites. The samples were characterized by SEM, XRD, BET, UV-Vis absorption, EPR and XPS. The results showed Ti3＋ defects were successfully doped in TiO2. The surface selective adsorption of hexavalent chromium [Cr2072 （Cr（VI））] and the desorption of trivalent chromium [Cr3＋ （Cr（III））] were investigated during the process ofphotocatalytic reduction positive charges due to more Ti3＋ defects on the surface show a Accordingly, the surface positive reduction of Cr（VI）. charges controlled by the Ti3＋ Zeta potential results presented that the increased significant improvement for adsorption of Cr（VI）. defects play important roles in the photocatalytic