摘要
浮法工艺生产平板玻璃,由于玻璃在锡槽内成形,玻璃下表面必然会引入一定的渗锡量,当渗锡量达到一定程度时,如果玻璃进行钢化加工,就会出现钢化彩虹,从而影响到玻璃的外观质量。分析了浮法玻璃钢化彩虹的形成与渗锡量的关系,提出了浮法玻璃生产中渗锡量的定性快速检测方法,可以避免玻璃在后续加工中造成损失;论述了降低玻璃渗锡量的措施,可用于指导浮法玻璃生产。
In float process,glass formed in tin bath,which caused of tin penetration. Tempering bloom would appear when glass that had tin infiltration over a certain amount was tempered,thus affecting the appearance quality of glass. In this paper,the relationship between the formation of tempering bloom and the amount of tin infiltration was analyzed. The rapid qualitative detection methods were recommended to avoid waste in subsequent processing. The measures to reduce the amount of tin infiltration were discussed to guide the glass production.
出处
《硅酸盐通报》
CAS
CSCD
北大核心
2017年第3期1035-1039,共5页
Bulletin of the Chinese Ceramic Society
关键词
玻璃
钢化彩虹
表面渗锡量
检测
glass
tempering bloom
amount of tin infiltration
detection