扫描电化学显微镜技术原位测Al-Mg合金在3.5% NaCl+5 mmol/L KI溶液中的腐蚀特性

Corrosion Behavior of Al-Mg alloy in 3.5% NaCl+ 5 mmol/L KI Solution In-situ Tested by SECM
下载PDF
导出
摘要 采用扫描电化学显微镜技术研究了Al-Mg合金在3.5%NaCl(质量分数)+5mmol/L KI溶液中的腐蚀行为,利用光学显微镜观察腐蚀后试样的表面形貌,用扫描电镜和能谱仪分析合金内金属间化合物成分,初步探讨Al-Mg合金的腐蚀机理。结果表明:Al-Mg合金表面不同区域活性溶解度不同,且腐蚀主要发生在金属间化合物与基体铝界面处;Al-Mg合金表面氧化电流峰的数量和数值随腐蚀时间延长而不断变化,说明在腐蚀过程中基体表面溶解是不均匀的,金属间化合物优先被腐蚀,144h后出现明显腐蚀坑。 The corrosion behavior of Al-Mg alloy in 3. 5wt. % NaCl - 5 mmol/L KI solution was investigated by scanning electrochemical microscopy (SECM). The surface morphology of the samples was observed by optical microscopy. The component of intermetallic compound was analyzed by scanning electron microscopy and energy dispersive spectroscopy. The corrosion mechanism of Al-Mg alloy was studied preliminarily. The results show that the dissolution was different in different regions of the surface of Al-Mg alloy, and the corrosion mainly occurred in the interface between intermetallic compounds and Al matrix. The quantity and value of oxidation peak current on the surface of Al-Mg alloy changed with prolongation of corrosion time, indicating that the surface dissolution was uneven in corrosion process. The intermetallie compounds were dissolved by corrosion first, and the corrosion pits appeared obviously after corrosion for 144 hours.
出处 《腐蚀与防护》 CAS 北大核心 2017年第4期282-286,共5页 Corrosion & Protection
基金 国家自然科学基金资助(51504111) 云南省自然科学基金(20113FA012 20113FB022)
关键词 AAl-Mg合金 扫描电化学显微镜技术 活性溶解 腐蚀 Al-Mg alloy scanning electrochemical microscopy (SECM) active dissolution corrosion
  • 相关文献

参考文献6

二级参考文献63

共引文献157

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部