In this paper the laser activities of a diode-pumped Yb:LuAG ceramic which was prepared by the solid-state reactive sintering method were reported. The maximum output power was 1.86 W in the continuous wave(CW) laser operation,corresponding to a slope efficiency of 53.6%. The CW laser could be tuned from 1030 to 1096 nm by inserting a prism in the cavity. With the assist of a semiconductor saturable absorber mirror(SESAM), passive mode-locking was realized,delivering sub-picosecond pulses with 933 fs duration and an average power of 532 m W at a repetition rate of 90.35 MHz.
In this paper the laser activities of a diode-pumped Yb:LuAG ceramic which was prepared by the solid-state reactive sintering method were reported. The maximum output power was 1.86 W in the continuous wave(CW) laser operation,corresponding to a slope efficiency of 53.6%. The CW laser could be tuned from 1030 to 1096 nm by inserting a prism in the cavity. With the assist of a semiconductor saturable absorber mirror(SESAM), passive mode-locking was realized,delivering sub-picosecond pulses with 933 fs duration and an average power of 532 m W at a repetition rate of 90.35 MHz.
基金
Project supported by the National Major Scientific Instruments Development Project of China(Grant No.2012YQ120047)
the National Key R&D Program of China(Grant No.2016YFB0402105)
the National Natural Science Foundation of China(Grant Nos.61205130 and 61575212)
the Key Research Project of the Frontier Science of the Chinese Academy of Sciences(Grant No.QYZDB-SSW-JSC022)